Abstract:Abstract Large surface area, high conductivity, and rich active site of carbon electrode materials are necessary characteristics for energy storage devices. However, high conductivity and high nitrogen doping of carbon electrode materials are difficult to coordinate. Here, a facile method via the carbonization of nitrogen‐containing Schiff base polymer has been developed to prepare high conductivity and high nitrogen‐doped hierarchical porous carbon. The organic components with a benzene ring structure in the polymer promote the formation of more sp2‐graphitized carbon, which is beneficial for the improvement of electrical conductivity. Nitrogen‐doped hierarchical porous carbon calcined at 900°C under the NH3 atmosphere possesses high nitrogen content of 7.48 at%, a large specific surface area of 1613.2 m2/g, and high electrical conductivity of 2.7 S/cm. As electrode materials in an aqueous‐based supercapacitor, nitrogen‐doped hierarchical porous carbon exhibits superior specific capacitance of 385 F/g at 1 A/g as well as excellent rate performance (242 and 215 F/g at a current density of 100 and 200 A/g, respectively). In addition, the specific capacitance of electrode measured in a two‐electrode system is 335 F/g at 1 A/g, and the long‐term cycling stability can be achieved with more than 94% initial capacitance after 10 000 cycles. The constructed symmetric supercapacitor delivers high energy density and high power density. The outstanding electrochemical performances combined with the novel and scalable synthetic approach make the nitrogen‐doped hierarchical porous carbon potential electrode material for electrochemical devices.

Nitrogen-doped hierarchical porous carbon as an efficient electrode material for supercapacitors

Facile 3D Nitrogen‐Doped Hierarchical Porous Carbon for High‐Performance Supercapacitors

Nitrogen-rich hierarchical porous hollow carbon nanofibers for high-performance supercapacitor electrodes

Highly Active N, O-doped Hierarchical Porous Carbons for High-Energy Supercapacitors

Nitrogen-functionalized Microporous Carbon Nanoparticles for High Performance Supercapacitor Electrode

Three-dimensional Nitrogen-Doped Hierarchical Porous Carbon Derived from Cross-Linked Lignin Derivatives for High Performance Supercapacitors

Nitrogen-doped macro-meso-micro hierarchical ordered porous carbon derived from ZIF-8 for boosting supercapacitor performance

Self-template and self-activation synthesis of nitrogen-doped hierarchical porous carbon for supercapacitors

Fabrication of high performance structural N-doped hierarchical porous carbon for supercapacitors

Nitrogen and Phosphorus Co-doped Porous Carbon for High-Performance Supercapacitors

Biomass-derived nitrogen-doped porous carbons with tailored hierarchical porosity and high specific surface area for high energy and power density supercapacitors

Nitrogen-doped micro-meso hierarchical porous carbon with electrochemical properties

Nitrogen‐doped Hierarchical Few‐layered Porous Carbon for Efficient Electrochemical Energy Storage

Molten Salt-Confined Construction of Nitrogen-Doped Hierarchical Porous Carbon for High-Performance Supercapacitors

Boosting the capacitive performance by constructing O, N co-doped hierarchical porous structure in carbon for supercapacitor

One pot synthesis of nitrogen-doped hierarchical porous carbon derived from phenolic formaldehyde resin with sodium citrate as activation agent for supercapacitors

A Nitrogen-doped Hierarchical Mesoporous/Microporous Carbon for Supercapacitors

Nitrogen-doped Hierarchically Ellipsoidal Porous Carbon Derived from Al-based Metal-Organic Framework with Enhanced Specific Capacitance and Rate Capability for High Performance Supercapacitors

Polymerization-Pyrolysis-Derived Hierarchical Nitrogen-Doped Porous Carbon for Energetic Capacitive Energy Storage

Nitrogen- and Oxygen-Containing Three-Dimensional Hierarchical Porous Graphitic Carbon for Advanced Supercapacitor

Acetone dissolution to prepare N-doped hierarchical porous carbon for supercapacitor