Hydrogen Isotope Effects in Ti$lt;inf$gt;1.0$lt;/inf$gt;Cr$lt;inf$gt;1.5$lt;/inf$gt;V$lt;inf$gt;1.7$lt;/inf$gt; Alloy

Yang Yong-Bin,Luo De-Li,Rao Yong-Chu,Guo Wen-Sheng

DOI: https://doi.org/10.15541/jim20160089

IF: 1.292

2016-01-01

Journal of Inorganic Materials

Abstract:Ti1.0Cr1.5V1.7 alloy was prepared by arc melting and then its morphology and constitution were analyzed by SEM and EDS. The observations showed that the alloy was unhomogeneous with some network-shaped precipitates. The structures of the hydrides of Ti1.0Cr1.5V1.7 were determined by XRD. The structures of the hydrides depended only on the hydrogen content, not on the kind of hydrogen isotopes. The dependences of separation factor (alpha(H-D)) on pressure, deuterium concentration and temperature were investigated systematically. Not significantly influenced by pressure, alpha(H-D) decreased with the increase of deuterium concentration. However, the dependence of alpha(H-D) on temperature was complicated. In 213-373 K, alpha(H-D) increased with the decrease of temperature, which agreed with the harmonic oscillator model (HOM). In 77-213 K, the experimental alpha(H-D) was different from the calculated value of HOM. According to the results of DSC measurement for the hydrides of Ti1.0Cr1.5V1.7 alloy, the disagreement between the experiments and the HOM in 77-213 K was not induced by phase transitions. Moreover, the maximum. alpha(H-D) reached 2.29 at 213 K.