Zn-Ti co-substituted LiZn microwave ferrites: Sintering characteristics and gyromagnetic properties
Mingchao Yang,Lijun Jia,Lun Xu,Penghui Yi,Yang Shen,Weile Fu,Zhihao Chen
DOI: https://doi.org/10.1016/j.jmmm.2024.172171
IF: 3.097
2024-05-23
Journal of Magnetism and Magnetic Materials
Abstract:To meet the low-loss and high-frequency application requirements of modern electronic information systems for integrated microwave devices, Zn-Ti co-substituted LiZn microwave ferrites were prepared in this work. The results demonstrated that Zn-Ti co-substitution promoted the grain growth and densification process during sintering, leading to a decrease in the pore-induced linewidth (Δ H p ) of LiZn composite microwave ferrites; the introduction of non-magnetic Zn 2+ and Ti 4+ ions lowered the content of Fe 3+ ions in the ferrites, which reduced the magnetocrystalline anisotropy constant | K 1 | and thus diminished the anisotropy-induced linewidth (Δ H a ). Besides, the dielectric loss of the material decreased with increasing Zn-Ti substitution amounts ( x ) due to the reduction of Fe 2+ ion content. As a result, when x = 0.35, the FMR linewidth was decreased from ∼ 251 Oe to ∼ 97 Oe, and the dielectric loss was greatly reduced from > 100 × 10 −4 to ∼ 3.82 × 10 −4 in the ferrites. The material also exhibited excellent properties including high saturation magnetization (∼3913 Gauss), high Curie temperature (∼304 °C), and low coercivity (∼2.05 Oe).
materials science, multidisciplinary,physics, condensed matter