Effect of hot rolling on microstructures and mechanical properties of SiC p /A356 aluminum matrix composites
Yajun Luo,Jiaxiong Yi,Mingzhe Chen,Li Zhou,Zhenlin Zhang,Zhonghua Huang,Xiaogang Sun,Yi Zhang,Liang Wen,Zhenggang Wu
DOI: https://doi.org/10.1016/j.jmrt.2024.09.201
IF: 6.267
2024-09-27
Journal of Materials Research and Technology
Abstract:This study focuses on the fabrication of SiC p /A356 aluminum matrix composites (AMCs) through stir casting and hot rolling, with the objective of investigating the effects of reduction on microstructural evolution and mechanical properties of SiC p /A356 AMCs. The composites were subjected to hot rolling at 500 °C for varying reduction levels of 30%, 50%, 70%, and 90%. As the reduction increased to 70%, the size of α-Al grains and SiC particle clusters increased. However, further reduction to 90% resulted in the flattening and elongation of α-Al grains, the dispersion of SiC particles into the grains, and a more uniform distribution of SiC particles. The relationship between reduction and SiC particle distribution was established. The ultimate tensile strength (UTS) and yield strength (YS) of SiC p /A356 AMCs showed a gradual increase with increasing reduction. The rolled composite with a 90% reduction exhibited the optimal combination of UTS, YS, and elongation (EL) values. Besides, the strengthening mechanisms were discussed and the dislocation strengthening has a significant contribution to the improvement of YS.
materials science, multidisciplinary,metallurgy & metallurgical engineering