Early Oxidation of Super304H Stainless Steel and Its Scales Stability in Supercritical Water Environments

Yanhui Li,Shuzhong Wang,Panpan Sun,Zhenxia Tong,Donghai Xu,Yang Guo,Jianqiao Yang

DOI: https://doi.org/10.1016/j.ijhydene.2016.04.144

IF: 7.2

2016-01-01

International Journal of Hydrogen Energy

Abstract:The early oxidation of Super304H stainless steel exposed to supercritical water at 450 degrees C, 540 degrees C, and 580 degrees C was characterized. After a 40 h exposure, distribution density of oxide grains produced on samples increased with experimental pressures, while initial aqueous pH had a negligible influence on short-term corrosion morphologies, implying that the outer oxide layer of scales may form via solid growth mechanism rather than by metals dissociation/oxides precipitation process. After a repeated 24 h cycles of exposure at condition of 540 degrees C/25 MPa followed by that of 500 degrees C/23 MPa up to 5 cycles, partial spallation of the scales appeared along inner and outer layer interface, not substrate/scales interface due to the enhanced adhesion of scales on the substrate by pinning effects and production and convergence of cavities at the inner/outer layer interface. (C) 2016 Hydrogen Energy Publications LLC. Published by Elsevier Ltd. All rights reserved.