Surface Topography in Peripheral Milling of Ti-6Al-4V: Multi-scale Evaluation and Fractal Analysis
Dong Yang,Tianhao Jia
DOI: https://doi.org/10.1007/s11665-023-09109-4
IF: 2.3
2024-01-03
Journal of Materials Engineering and Performance
Abstract:Ti-6Al-4V alloy has been widely used in aerospace and other fields with its excellent mechanical properties, but its poor machinability makes the surface quality difficult to control, which is reflected in multi-scale surface topography features. The peripheral milling-induced surface topography of Ti-6Al-4V was evaluated by statistical and fractal analyses methods at different scales. Firstly, the macro- and microdefects characteristics of the machined surface and their formation mechanisms were clarified. And then, the response laws of profile, height and spatial surface roughness and fractal characteristics with peripheral milling parameters (spindle speed n , radial depth of cut a e , and feed rate f ) at different scales were revealed. The results show that the natural defects are distinguished by larger-scale features, such as feeding marks and scratches, whereas the random defects are smaller-scale features, including adhered particles, random scratches, and cracks. Lower arithmetical mean deviation and maximum height are obtained at n = 900 rev/min, a e = 0.5 mm, and f = 0.06 mm/rev, at the observation scales of 200 × and 400 ×. And all surface roughness parameters showed high variability at 1000 ×. The kurtosis and skewness of the peripheral milling surface show that there are no extreme peaks and valleys. A larger fractal dimension was obtained at n = 1150 rev/min, a e = 0.3 mm, and f = 0.06 mm/rev, due to surface defects making the surface structure more complex. The variation trend of the fractal characteristics, including irregularity and self-similarity, on the Ti-6Al-4V alloy surface with peripheral milling parameters is independent of the observation scale, equipment resolution, and sampling length.
materials science, multidisciplinary