Abstract:This paper investigated the appearance, microstructure, and mechanical properties of laser welded joints for 1700-MPa, ultrahigh-strength steel (UHSS) with 6 mm thickness. The results indicate welding speed was the dominant factor that affected appearance quality. A sound weld without underfill can be obtained when the speed was limited to approximately 2-3 m/min. Two softening mechanisms exist in the heat-affected zone (HAZ). In the intercritical heat affected zone (ICHAZ), ferrite appears and the hardness drops sharply. For the subcritical heat-affected zone (SCHAZ), the microstructure was tempered martensite with precipitation of carbides and the high temperature temper results in the minimum hardness. With a martensitic structure in the weld metal and a narrow softening zone in the HAZ, more than a 94% joint efficiency was achieved in tensile testing. Only about a 40-deg maximum bending angle was obtained during a bend test, as plastic deformation mainly concentrates in the softening zone due to nonuniform hardness distribution. The study also found that the existence of porosities in the joints had significant affects on the ductility, toughness, and fracture mechanism, but little affect on the joint strength. For the joints without porosities, the fractures from tensile and bend tests both initiated at the zone with the minimum hardness and propagated along the 45-deg direction. But when porosities existed in the joints, fractures occurred completely in the weld metal, which resulted in a smaller elongation and bending angle as well as impact energy. However, the tensile strength was similar to an average value.

Effect of Pulse Frequency on Microstructure and Properties of Welded Joints for Dual Phase Steel by Pulsed Laser Welding

Effect of pulse frequency on the nanosecond pulsed laser welded Al/steel lapped joint

Effect of pulse frequency on laser welding on SiCp/6061 aluminum alloys with powder

Effect of pulse overlap rate on the microstructure and mechanical properties of laser welds of thin AZ31 magnesium alloy

Effect of pulse energy on microstructure and properties of laser lap-welding Hastelloy C-276 and 304 stainless steel dissimilar metals

Effects of Pulsing Parameters on Weld Shape Parameters During Pulsed Nd-YAG Laser Welding of Aluminum Alloys

Microstructure and Mechanical Properties of Pulsed Laser Welded Al/steel Dissimilar Joint

Impact of microstructure evolution on the corrosion behaviour of the Ti–6Al–4V alloy welded joint using high-frequency pulse wave laser

Effect of pulse frequency on microstructure and properties of Ti-6Al-4V by ultrahigh-frequency pulse gas tungsten arc welding

Microstructure and corrosion resistance of fusion zone in Ti-6Al-4V alloy welded using pulsed- and continuous-wave lasers

Microstructure and Mechanical Properties of Fiber Laser Welded QP980/press-hardened 22mnb5 Steel Joint

A Study of the Performance of Dissimilar Pulsed-Laser-Welded JSC590R/JAC980YL Steel Joints of Differential Thickness

Mirostructure and Properties of Laser Welded Joints of Dual Phase and Press-Hardened Steels

Microstructure- and Strain Rate-Dependent Tensile Behavior of Fiber Laser-Welded DP980 Steel Joint

Development of Weld Metal Microstructures in Pulsed Laser Welding of Duplex Stainless Steel

Fiber Laser Welding of 1700-MPa, Ultrahigh-Strength Steel

Effect of Heat Input on Microstructure and Mechanical Properties of Laser Welded Medium Mn Steel Joints

Microstructure and Mechanical Properties of Fe-36Ni and 304L Dissimilar Alloy Lap Joints by Pulsed Gas Tungsten Arc Welding

Microstructure and Mechanical Properties of Nanosecond Pulsed Laser Welded Al–Cu–steel Laminated Structures

Microstructure and Mechanical Properties of Laser Fusion Welded Al/steel Joints Using a Zn-based Filler Wire

Melt Flow and Microstructural Characteristics in Beam Oscillation Superimposed Laser Welding of 304 Stainless Steel