Abstract:A combined steady-state and transient approach is employed to investigate the corrosion behavior of X80 pipeline steel in carbon dioxide-saturated brines. Continuous bubbling of carbon dioxide into a test vessel with 1 liter capacity is performed to simulate the flowing condition. The measurement of time-dependent open-circuit potential, polarization resistance, and electrochemical impedance spectroscopy (EIS) is conducted to interpret the evolution of dissolution processes at the corroding interface. Three distinguishing stages are observed at a temperature of 60 °C during a whole exposure of 144 h. Analyses mainly based on the consecutive mechanism show that after the first stage of the active-adsorption state, the anodic reaction is significantly retarded by the accumulation of (FeOH)ads on the iron surface, causing a sharp increase in the polarization resistance and the open-circuit potential, as well as the disappearance of the inductive loop in EIS. At the third stage, the formation of the corrosion product layer similarly reduces both the anodic and cathodic reactions, which arouses a linear increase in the polarization resistance with time and a capacitive loop in EIS but changes the open-circuit potential slightly. An increase in salinity in this study reduces the polarization resistance and enhances iron dissolution by promoting the formation and relaxation of (FeOH)ads; however, it brings little change to the developing time of the three stages obviously. At a low temperature of 20 °C, a protective product layer is not observed in carbon dioxide-saturated brine, and the dissolution of iron is mainly under activation control during the whole exposure. A notable enlarged polarization resistance and different interfacial processes are observed in an alkaline solution compared with those in acidic environments, which is deduced to be resulted from an impedance in the relaxation of (FeOH)ads by increasing pH. The observations in this study support well that the iron dissolution reaction at the initial stage exposed in carbon dioxide aqueous environments is dominant by water adsorption on the iron surface, and further investigation should be performed on the role that carbon dioxide plays in the evolution of corrosion products and the formation of a protective film on the steel surface by taking into account local water chemistry.

INFIUENCE OF TEMPERATURE AND SULFUR ION ON CARBON DIOXIDE CORROSION BEHAVIOR OF N80 STEEL

EFFECT OF TEMPERATURE ON PROPERTIES OF CO2 CORROSION SCALE OF N80 CARBON STEEL

Revealing the Effect of O2, SO2 and H2O in Supercritical CO2 on the Corrosion Behavior of 316L Steel at Elevated Temperature

EFFECT OF CHLORIDE ION ON CORROSION BEHAVIOR OF N80 STEEL IN CO2 SOLUTIONS

Study on Corrosion Characteristics of Heat-resistant Materials in Supercritical Carbon Dioxide Environment Containing Oxygen Impurities

Characteristics of CO2 corrosion scale formed on N80 steel in stratum water with saturated CO2

Influences of Temperature and pH Value on the Corrosion Behaviors of X80 Pipeline Steel in Carbonate/Bicarbonate Buffer Solution

Insights into the effect of H2S on the corrosion behavior of N80 steel in supercritical CO2 environment

Investigation on CO2 corrosion behaviors of N80 tubing steel under stress conditions

Synergistic Effect of O2 and H2S on the Corrosion Behavior of N80 Steel in a Simulated High-Pressure Flue Gas Injection System

Impact of SO2 Concentration on the Corrosion Rate of X70 Steel and Iron in Water-Saturated Supercritical CO2 Mixed with SO2

Influence of FeCO 3 and FeSO 4 Layers on Corrosion in Sulfuric Acid Medium of Eutetoid Steels

The Impact of Temperature on CO2 Corrosion and the Formation of Corrosion Product Film

Effect Of Temperature On Corrosion Behaviour Of X70 Steel In High Pressure Co2/So2/O-2/H2o Environments

INFLUENCE OF TEMPERATURE,CO_2 PARTIAL PRESSURE, FLOW RATE AND pH VALUE ON UNIFORM CORROSION RATE OF X65 PIPELINE STEEL

ENVIRONMENTAL FACTORS CONTROLLING EARLY CORROSION PERFORMANCE OF CARBON STEEL UNDER LIQUID LAYER CONTAINING SO42

Effect of Temperature on Corrosion Behavior and Mechanism of S135 and G105 Steels in CO2/H2S Coexisting System

Experimental Investigation on Corrosion Behavior of X80 Pipeline Steel under Carbon Dioxide Aqueous Conditions

The corrosion behaviour of sulphur on the carbon steel used in oil & gas field with high concentration of H2S

Effect of H2S concentrations on corrosion failure of L245NS steel in CO2-O2-H2S system

Characterization Of The Surface Film Fonned From Carbon Dioxide Corrosion On N80 Steel