Abstract:A combined steady-state and transient approach is employed to investigate the corrosion behavior of X80 pipeline steel in carbon dioxide-saturated brines. Continuous bubbling of carbon dioxide into a test vessel with 1 liter capacity is performed to simulate the flowing condition. The measurement of time-dependent open-circuit potential, polarization resistance, and electrochemical impedance spectroscopy (EIS) is conducted to interpret the evolution of dissolution processes at the corroding interface. Three distinguishing stages are observed at a temperature of 60 °C during a whole exposure of 144 h. Analyses mainly based on the consecutive mechanism show that after the first stage of the active-adsorption state, the anodic reaction is significantly retarded by the accumulation of (FeOH)ads on the iron surface, causing a sharp increase in the polarization resistance and the open-circuit potential, as well as the disappearance of the inductive loop in EIS. At the third stage, the formation of the corrosion product layer similarly reduces both the anodic and cathodic reactions, which arouses a linear increase in the polarization resistance with time and a capacitive loop in EIS but changes the open-circuit potential slightly. An increase in salinity in this study reduces the polarization resistance and enhances iron dissolution by promoting the formation and relaxation of (FeOH)ads; however, it brings little change to the developing time of the three stages obviously. At a low temperature of 20 °C, a protective product layer is not observed in carbon dioxide-saturated brine, and the dissolution of iron is mainly under activation control during the whole exposure. A notable enlarged polarization resistance and different interfacial processes are observed in an alkaline solution compared with those in acidic environments, which is deduced to be resulted from an impedance in the relaxation of (FeOH)ads by increasing pH. The observations in this study support well that the iron dissolution reaction at the initial stage exposed in carbon dioxide aqueous environments is dominant by water adsorption on the iron surface, and further investigation should be performed on the role that carbon dioxide plays in the evolution of corrosion products and the formation of a protective film on the steel surface by taking into account local water chemistry.

Characterization Of The Surface Film Fonned From Carbon Dioxide Corrosion On N80 Steel

Characterization of the surface film formed from carbon dioxide corrosion on N80 steel

Characteristics of CO2 corrosion scale formed on N80 steel in stratum water with saturated CO2

Revealing the Effect of O2, SO2 and H2O in Supercritical CO2 on the Corrosion Behavior of 316L Steel at Elevated Temperature

Properties of Surface Film on XT0 Pipeline Steel in CO2-3/HCO-3 Environment

Corrosion Behavior of J55 and N80 Carbon Steels in Simulated Formation Water under Different CO2 Partial Pressures

Investigation on CO2 corrosion behaviors of N80 tubing steel under stress conditions

Properties of Surface Film on X70 Pipeline Steel in CO3^2-／HCO3^- Environment

Properties of surface film on X70 pipeline steel in CO32-/HCO3- environment

Wear Behavior of CO2 Corrosion Scales on Well Tube Steel N80 in Water-Sand Two-Phase Fluid Medium

Experimental Investigation on Corrosion Behavior of X80 Pipeline Steel under Carbon Dioxide Aqueous Conditions

Corrosion Behavior of Oil Tube Steels under Conditions of Multiphase Flow Saturated with Super-Critical Carbon Dioxide

Research of CO_2 Corrosion Kinetics of Tubing and Casing Steel P110

CO2 Corrosion Behavior of High-Strength and Toughness V140 Steel for Oil Country Tubular Goods

EIS study of the surface film on the surface of carbon steel from supercritical carbon dioxide corrosion

Corrosion Behavior of X65 Steel in Carbon Dioxide Solution under High Temperature and High Pressure

A study by electrochemical impedance spectroscopy and surface analysis of corrosion product layers formed during CO2 corrosion of low alloy steel

Long term corrosion of X70 steel and iron in humid supercritical CO 2 with SO2 and O2 impurities

Long term corrosion of X70 steel and iron in humid supercritical CO2with SO2and O2impurities

Study of Carbon Dioxide Corrosion Products by X-Ray Diffraction

Electrochemical Investigation of the Corrosion of Different Microstructural Phases of X65 Pipeline Steel under Saturated Carbon Dioxide Conditions