HE ELECTICAL-RANSPORT PROPERTIES OF THE MO-DOPING La0.7Ca0.2Ba0.1Mn1-xMoxO3
CAO Yong-zhen,MEI Ye,LIU Bao-qin,LIU Zhen-hua,LIN Xiao,XU Zhu-an,HE Jun-hui
2010-01-01
Abstract:The Mo-doping La0.7Ca0.2Ba0.1Mn1-xMoxO3(x=0,0.01,…,0.06) polycrystalline samples have been prepared by solid state reaction method. The influence of Mo-doping on the structure ,transport properties and magnetoresistance have been investigated. X-ray diffraction indicated that all of the samples have orthorhombic(Pbnm) perovskite structure. The magnetization versus temperature (M～T) curves for zero field-cooled (ZFC)and field-cooled (FC) conditions in a magnetic filed of 100 G suggest that all of the samples undergo a FM to PM phase transition. The cluster-glass state is found to be formed below Tc,meanwhile the transition temperature Tc decreases from Tc~294.2K(x=0.00) to Tc~240.83K (x=0.06) due to increasing Mo doping. The temperature dependence of resistivity ρ(T) curves are measured under H=0T and H=1.5T,which reveals a metal-insulator transition and the transition temperature TP shifts obviously to lower temperature with increasing Mo content. The temperature dependence of magnetoresistance(MR ) curve of the samples indicates that the CMR around Tp is enhanced considerably by Mo-doping. For the sample with x=0.06,MR reaches a maximum value of 45.32%,which is almost three times of the undoped sample for x=0.