Abstract:Tensile stress-strain testing is used to investigate fracture behavior of carbon black-reinforced styrene-butadiene rubber, using 50 replicate specimens. Four vulcanized rubber compounds are studied: a CB-filled SBR with standard mixing conditions (Control); the same formulation with intentional poor mixing of the CB; and materials identical to the control material but formed by adding minor amounts of 0.5 mm diameter glass microspheres (beads) – serving as large model defects/inclusions - using a two-roll mill at two levels corresponding to average values of 0.78 and 6.24 beads per gauge section region of the tensile test specimen. This paper focuses on microscopy analysis of the resulting fracture surfaces to complement our recent publication on Weibull failure statistics for distributions of tensile strength and crack precursor size (Polymers 12, 203 (2020)). All 200 fractured specimens from tensile testing at 23°C are imaged with light microscopy and exhibit fracture surfaces that are characterized by relatively smooth planes that are perpendicular to the uniaxial loading direction. The majority of tensile failures originate from the edges of the dumbbell specimens, in line with expectations from fracture mechanics. Light microscopy reveals concentric fracture ring features of high specular reflectance emanating from crack precursors, which are a universal feature of the failure process for these compounds and independent of precursor type, size, or location. Non-contact interferometric microscopy confirms that the rings are the result of variations in surface micro-roughness; proceeding outwards from the precursor as rough-smooth-rough to the edge of the fracture surface. Fracture rings are also observed for tensile tests performed at 80°C. The variation in surface roughness of the fracture surface has parallels to the stick-slip tearing behavior seen for rubbers torn at medium to high rates. To the best of the authors’ knowledge, this is the first time that such striking features have been reported.

Research Progress in Crack Propagation of Rubber Composites

Experimental Characterization and Finite Element Modeling the Deformation Behavior of Rubbers with Geometry Defects

Characterization and Quantitative Analysis of Crack Precursor Size for Rubber Composites.

Crack Growth Mechanism of Styrene-Butadiene Rubber Filled with Silica Nanoparticles Studied by Small Angle X-ray Scattering

CRACK DAMAGE AND GROWTH BEHAVIOR OF BRAIDED COMPOSITE

Study on the evolution law and quantitative characterization of micro-crack propagation in the compressive failure process of rocks

Strain Induced Crack Initiation and the Subsequent Crack Propagation of Fiber-Reinforced Resin Composites

A MICROSCOPY INVESTIGATION OF RUBBER COMPOUND CRACK PRECURSORS AND TENSILE FRACTURE SURFACES

THE STUDY ON TESTS AND NUMERICAL SIMULATION OF CRACK PROPAGATION PROBLEM IN DELAMINATION FAILURE OF COMPOSITE LAMINATED PLATE

Effect of Microcracks on the Tensile Properties of 3D Woven Composites

Relationship Between Dynamic Fatigue Crack Propagation Properties and Viscoelasticity of Natural Rubber/silicone Rubber Composites

Mechanical properties and damage evolution characteristics of composite rock mass with prefabricated fractures

Experimental and numerical study on crack propagation and coalescence in rock-like materials under compression

A Study of the Propagation of an Embedded Crack in a Composite Laminate of Finite Thickness

Evolutionary trace for ductile fracture performance of rubber−cement composites

Compressive Failure of Fiber Reinforced Polymer Composites by Imperfection

Quantitative statistical analysis of the crack propagation and fracture process of self‐compacting rubber concrete based on acoustic emission

Study on the Crack Evolution Process and Stress Redistribution Near Crack Tip in Soil

Frictional Sliding of Microcracks under Compression

Research Progress in Damage Evolution of Woven Composites

Thermo-mechanical coupling analysis of edge-cracked rubber specimen focusing on the crack tip: Experimental observation and numerical simulation