Influence of gadolinium content on magnetic property and oxidation mechanism of Fe-B-Nb-Gd metallic glasses
Mi Xiao-Lei,Hu Liang,Wu Bo-Wen,Long Qiang,Wei Bing-Bo,
DOI: https://doi.org/10.7498/aps.73.20232040
IF: 0.906
2024-01-01
Acta Physica Sinica
Abstract:In this work, we used the rapid solidification technique to prepare five kinds of metallic glasses with different Gd contents. The correlation between the element Gd and the glass-forming ability, thermal stability, and magnetic properties of (Fe 73 B 22 Nb 5 ) 100-x Gd x (x=0, 0.5, 1, 1.5, 2) alloys were deeply investigated. By comparing the microstructural morphology and solute distribution of oxidation products before and after adding Gd, the amorphous oxidation mechanism was analyzed systematically. With the addition of Gd, the atomic size difference of the alloys exceeds 13%, and the configuration entropy increases from 7.27 kJ·mol -1 ·K -1 to 9.44 kJ·mol -1 · K -1 . The glass-forming ability of the alloy has been significantly improved. The increase in Gd content increases the glass transition temperature of the alloy to 864 K, and the supercooled liquid region can reach 73 K, significantly enhancing the thermal stability of the metallic glasses. Gd limits the local anisotropy of the alloy and reduces the density of quasi-dislocation dipole defects. This can effectively reduce the pinning sites that hinder the rotation of magnetic domain walls, thereby improving the soft magnetic property. By comparing with the metallic glasses without Gd, only 2 at.% Gd can reduce the coercivity by 8%. Moreover, Gd makes the metallic glasses more sensitive to temperature variation during the oxidation process, and the temperature of the maximum oxidation rate is reduced by 15K. However, their antioxidant performance did not deteriorate. The Gd atoms are influenced by binding energy and migrate to the surface, forming Gd-rich oxides. They fill surface defects and occupy a large amount of top space, leading to the structure near the surface more compact. This structure reduces the channels for oxygen atoms to diffuse through the microstructure interface, which helps to improve antioxidant ability. This work provides a new approach for designing high performance Fe-based metallic glasses.
physics, multidisciplinary