Inhibitory Effect of Silicon on the Steel/Aluminum Rolling Composite Interface Compound

Chao GAO,Ming GAO,Ping WANG

DOI: https://doi.org/10.3969/j.issn.1673-5862.2010.02.015

2010-01-01

Abstract:We have a systematic study to steel-aluminum composite materials' interface compounds at high-temperature and find some way to inhibit the generation of interface compounds.To obtain high-quality composites,it is necessary on the high-temperature to inhibit the generation of the interface compounds,to improve the bounding strength of steel-aluminum and processing performance.By adding silicon into aluminum material that is used to prepare composite material of steel/aluminum,and by cold-rolled composite technology,we studied the inhibition of silicon on composite interface compounds.The composite material samples with different contents of Si were compared in groups.Their microstructures were analyzed by using metallographic microscope and SEM.The results show that steel/aluminum composite materials' interface compounds belong to Fe-Al compounds,the majority is Fe2Al5.We calculated interface free energy through analysis of the thermodynamic calculation,and found that iron-silicon compounds was more prone to generate than iron-aluminum compounds in the annealing process,and a certain quantity of silicon added into aluminum can apparently restrain the production of steel/aluminum interface compounds,the inhibitory effect was more obvious with the increasing of silicon content.