The synergistic mechanism of ultrasonic and heat treatment on the composite structure and mechanical properties of Nb-Si-Zr based in-situ composites
Chaowen Zheng,Qi Wang,Ruirun Chen,Wei Wei,Yanqing Su,Hengzhi Fu
DOI: https://doi.org/10.1016/j.jallcom.2024.176816
IF: 6.2
2024-10-13
Journal of Alloys and Compounds
Abstract:Ultrasonic assisted solidification (UST), heat treatment and alloying are all effective methods to control the microstructure of materials and improve their properties. In this paper, the Nb-16Si-20Zr-2C- x W composites were prepared using ultrasonic assisted solidification technology of high temperature melt (≥1800°C) and heat treatment. The influence mechanism of ultrasonic, the W element, and the synergistic regulation mechanism of ultrasonic and heat treatment on the material were studied. Nb-16Si-20Zr-2C- x W(UST) alloys are mainly composed of Nbss phase and γNb 5 Si 3 phase, and their microstructures are mainly divided into strong active zone(SZ) and weak active zone(WZ). In the Nb-Si superalloy melt treated by ultrasonic wave, the area near the ultrasonic sound source is the strong active zone, while the area far away from the ultrasonic sound source is the weak active zone. The features of faceted primary phases and non-faceted primary phases in the SZ and WZ are explained by the equation of undercooling degree at different interfaces and effect of ultrasonic on component undercooling. As the W element content in the alloys (UST) increases, the content of the Nbss phase increases, the median diameter of the primary γNb 5 Si 3 phase decreases, and the room temperature fracture toughness and compressive strength show an upward trend. When the addition amount of W element reaches 2 at%, there are more crack deflections, crack bridging and secondary cracks in the crack propagation path. Through the special arrangement of primary γNb 5 Si 3 phase in the ultrasonic field, the energy density of ultrasonic waves in the melt is calculate to be 33.5 kW/m 2 . The microstructure of Nb-16Si-20Zr-2C- x W alloys(UST+HT) became more uniform and spheroidize. It is worth mentioning that there are plenty of long strip γNb 5 Si 3 phases with different orientations in the Nb-16Si-20Zr-2C-0.1W(UST+HT) alloy and the long strip γNb 5 Si 3 phases with the same orientation are arranged in a periodic manner. This special composite structure induces crack deflections and branching cracks when cracks propagation, so the room temperature fracture toughness of Nb-16Si-20Zr-2C-0.1 W (UST+HT) alloy reaches 15.66 MPa·m 1/2 .
materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering