Abstract:In this work, a facile hydrothermal route has been presented for the hierarchical growth of CdSe dendritic nanostructures by varying reducing agent (hydrazine hydrate) volume % in the presence of EDTA as a complexing agent. The morphological transition from spherical to dendritic form has demonstrated remarkable improvement in the field emission performance of CdSe. The X-ray diffraction analysis indicates the formation of highly crystalline CdSe nanostructures with average crystallite size of about 13–18 nm which is well supported by Raman spectroscopy. Further, X-ray photoelectron spectroscopy and energy-dispersive X-ray spectroscopy analyses confirm the elemental composition of optimized material. The morphology of synthesized materials is confirmed by field emission scanning electron microscopy and transmission electron microscopy techniques. The optical analysis with UV–Vis spectroscopy (DRS mode) shows the band gap variation in the range of 1.68–1.71 eV and photoluminescence emission spectra display high-intensity band-edge emissions peak centred at 678 nm. Field emission studies indicate that the value of turn-on field for CdSe nanostructures is lowered from 5.4 to 3.75 V/μm (at 1 μA/cm 2 ) with a reduction in threshold field value from 6.9 to 5.5 V/μm (at 10 μA/cm 2 ) as an effect of morphological variation. The maximum current density shows a considerable rise to 92 μA/cm 2 (at applied field 8.2 V/μm) from the initial value of 28 μA/cm 2 (at 7.9 V/μm). Further, the promising field enhancement factor of 4016 is observed for CdSe dendritic nanostructures. Investigations presented herein clearly show the potential of synthesized material for field emission-based vacuum micro-electronic applications.

Morphology-Controlling and Growth Mechanism of Hierarchical CdS Dendrites

Synthesis and Characterization of Large-Scale Hierarchical Dendrites of Single-Crystal CdS

Biomolecule-Assisted Hydrothermal Synthesis Of Hierarchical Cds Dendrites

Biomolecule-Assisted Synthetic Route to Nanostructured Crystals: Synthesis of CdS Hierarchical Dendrites

Hydrothermal Synthesis, Characterization And Growth Mechanism Of Single Crystal Lead Titanate Pyrochlore Dendrites

Controlling Crystallization and Morphologies of Monoclinic Bismuth Vanadate (bivo4) Dendrite with Enhanced Photocatalytic Activities

Preparation and Growth Mechanism of CdS Nanorods via Chemical Bath Deposition

Synthesis Of 3-D Hierarchical Dendrites Of Lead Chalcogenides In Large Scale Via Microwave-Assistant Method

HYDROTHERMAL SYNTHESIS OF DENDRITE-LIKE ZINC SULFIDE CRYSTALS

Controllable growth of dendrite-like CuO nanostructures by ethylene glycol assisted hydrothermal process

A Dry Method To Synthesize Dendritic Ag2se Nanostructures Utilizing Cdse Quantum Dots And Ag Thin Films

Crystallization of Amorphous Colloids: an Effective Approach for the Rapid and Large-Scale Preparation of Antimony Sulfide Dendrites

Study on the Morphology Control of CdS Nanocrystals Synthesized by Hydrothermal Method

Surfactant-Free Fabrication of Catio3 Butterfly-Like Dendrite Via A Simple One-Step Hydrothermal Route

Growth of PbS crystals from nanocubes to eight-horn-shaped dendrites through a complex synthetic route

Novel hierarchical CdS crystals by an amino acid mediated hydrothermal process

Synthesis of highly crystalline silver dendrites microscale nanostructures by electrodeposition

Diameter- and current-density-dependent growth orientation of hexagonal CdSe nanowire arrays via electrodeposition.

Novel three-dimensional Co3O4 dendritic superstructures: Hydrothermal synthesis, formation mechanism and magnetic properties

Controlled Synthesis of PbWO4 Dendrites by a Simple Sonochemical Method

Hierarchical growth of CdSe dendritic nanostructures for enhanced field emission application