Abstract:Ni x Cu0.2Zn y Fe1.98O4 (x = 0.16, 0.26, 0.35, 0.43, 0.50; y = 0.8−x) ferrites were prepared via solid-state reaction. The influence of Ni2+ concentration on ferrites composition, microstructure, magnetic properties and DC-bias superposition characteristics was studied by XRD, SEM, XPS, and VSM. Then, the effect of magnetic properties on the DC-bias superposition characteristics was analyzed. The results showed that the ferrites sintered at 900 °C for 3 h were all in pure spinel phase with an average grain size of 7.5 μm and a relative density of about 5.15 g cm−3. With the increase in Ni2+ concentration, the saturation magnetization (M s ) and coercivity (H c ) of ferrites increased, but the magnetocrystalline anisotropy constant (K 1 ) first increased and then decreased. And the M s , H c , and K 1 of the specimen with x = 0.43 were 63.62 emu·g−1, 27.36 Oe, and 1813.17 Oe·emu·g−1, respectively. In particular, the specimen of x = 0.50 achieved the best DC superposition characteristics, where the H 70% was about 220 A m−1. The incremental permeability of the specimens decreased rapidly at a bias magnetic field <400 A m−1. The variation mainly originated from the domain wall displacement, and the rate of decrease was influenced by both M s and K 1 . At a bias magnetic field ≥400 A m−1, the incremental permeability of the specimens decreased slowly, mainly because the number of domain walls decreased until disappearing, and the specimens tended to become a single domain structure. And the rate of decrease of incremental permeability was mainly affected by K 1 .

Structure and Dielectric Properties of Cu Ion-substituted Ni-Zn Ferrites

Effect of Cu ion substitution on structural and dielectric properties of Ni–Zn ferrites

Effect of Zn Substitution on Morphology and Magnetic Properties of Cufe2o4 Nanofibers

Investigation on Nickel Concentration Dependence Structural, Dielectric and Magnetic Properties of Ni–Zn Ferrites

Gyromagnetic properties of Cu-substituted NiZn ferrites for millimeter-wave applications

Improvement in Structural and Magnetic Properties of Electrospun Ni1-xCuxFe2O4 Nanofibers

Effect of Copper Substitution on the Dielectric and Magnetic Properties of Low-Temperature-Sintered Z-type Ferrites

Synthesis and investigation of structural, morphological, magnetic, dielectric and impedance spectroscopic characteristics of Ni-Zn ferrite nanoparticles

Structure, Morphology, and Magnetic Properties of High-Performance NiCuZn Ferrite

Effects of Microstructure on the Temperature Dependence of Relative Initial Permeability of NiCuZn Ferrites

The influence of Lu substitution on the Microstructure, electromagnetic Properties, and impedance of NiZnCo ferrite

Microstructure, magnetic, and power loss characteristics of low‐sintered NiCuZn ferrites with La2O3‐Bi2O3 additives

Effect of Divalent Metal Ions Substitution on the Magnetic Properties of Ba3Co2-Me Fe24O41 (me = Zn2+, Ni2+) Hexagonal Ferrites

Microstructure and magnetic properties of Ni–Zn ferrite ceramics with different Ni2+ contents

Effects of Ni2+ concentration on the composition, structure, magnetic properties, and DC-bias superposition characteristics of NiCuZn ferrites

Investigation of structural and magnetic properties of Sn-substituted NiZn spinel ferrites

Influence of Nd substitution on the structural, magnetic and electrical properties of NiZnCo ferrites

The Influence of Nd 3+ Ions Doping on Structural, Dielectric and Magnetic Properties of Ni–Zn Ferrites

Effect of Zn substitution on morphology and magnetic properties of copper ferrite nanofibers

Magnetic and Electrical Properties of Low-Temperature Sintered Mn-doped NiCuZn Ferrites

Influence of Ti4+ substitution on the structural, magnetic, and dielectric properties of Ni-Cu–Zn ferrite