Effects of Ni2+ concentration on the composition, structure, magnetic properties, and DC-bias superposition characteristics of NiCuZn ferrites
Deng-ming Wu,Xiao-pan Liu,Peng-zhao Gao,Luo-ting He,Jian-wei Li
DOI: https://doi.org/10.1016/j.ceramint.2021.12.343
IF: 5.532
2022-04-01
Ceramics International
Abstract:Ni x Cu0.2Zn y Fe1.98O4 (x = 0.16, 0.26, 0.35, 0.43, 0.50; y = 0.8−x) ferrites were prepared via solid-state reaction. The influence of Ni2+ concentration on ferrites composition, microstructure, magnetic properties and DC-bias superposition characteristics was studied by XRD, SEM, XPS, and VSM. Then, the effect of magnetic properties on the DC-bias superposition characteristics was analyzed. The results showed that the ferrites sintered at 900 °C for 3 h were all in pure spinel phase with an average grain size of 7.5 μm and a relative density of about 5.15 g cm−3. With the increase in Ni2+ concentration, the saturation magnetization (M s ) and coercivity (H c ) of ferrites increased, but the magnetocrystalline anisotropy constant (K 1 ) first increased and then decreased. And the M s , H c , and K 1 of the specimen with x = 0.43 were 63.62 emu·g−1, 27.36 Oe, and 1813.17 Oe·emu·g−1, respectively. In particular, the specimen of x = 0.50 achieved the best DC superposition characteristics, where the H 70% was about 220 A m−1. The incremental permeability of the specimens decreased rapidly at a bias magnetic field <400 A m−1. The variation mainly originated from the domain wall displacement, and the rate of decrease was influenced by both M s and K 1 . At a bias magnetic field ≥400 A m−1, the incremental permeability of the specimens decreased slowly, mainly because the number of domain walls decreased until disappearing, and the specimens tended to become a single domain structure. And the rate of decrease of incremental permeability was mainly affected by K 1 .
materials science, ceramics