Abstract:Nickel-copper-zinc (NiCuZn) ferrites with high permeability and low magnetic loss have high application potential in high-frequency electronics. In this work, NiCuZn ferrite samples with different Cu contents were prepared by a two-step sintering method. First, the optimal temperatures of the two-step sintering method (1025/925 °C) were confirmed, thereafter the influence of the Cu content on the crystal structure, microstructure, magnetic and dielectric properties of NiCuZn ferrite were studied in detail. Structural characterization showed that an increase in Cu content promoted grain growth and resulted in NiCuZn ferrites with a denser microstructure and decreased porosity. However, a second phase of CuO formed once the content of Cu (x value) reached 0.16. The magnetic hysteresis loops revealed that the saturation magnetization increased as x increased and the highest value of 57.3 emu/g was obtained at x = 0.14. The dielectric property measurement showed that increasing the Cu content could improve the dielectric constant and reduce the dielectric loss. The permeability measurements showed an increase in permeability with Cu content from x = 0.10 to x = 0.14 and a decrease when x = 0.16. Consequently, a NiCuZn ferrite with an appropriate microstructure and with high permeability (μ'=855), low magnetic loss (tanδμ = 0.02), and high saturation magnetization (57.3 emu/g) could be obtained at a Cu content of x = 0.14 and sintering temperatures of 1025/925 °C in the two-step sintering method. This NiCuZn ferrite provides new guidance for developing RF frequency multilayer inductors.

Microstructure, magnetic, and power loss characteristics of low‐sintered NiCuZn ferrites with La2O3‐Bi2O3 additives

Effect of Bi2O3 and Co2O3 co-doping on power loss characteristics of low-temperature-fired NiCuZn ferrites

Sintering, Microstructure and Magnetic Properties of Low Temperature Co-Fired NiCuZn Ferrites with Nb2O5 and MoO3 Additions

Investigation on the Micro-Structure and Magnetic Properties of LMZBS-Bi2O3 Doped Low-Temperature Sintered NiCuZn Ferrites

The Effect of Sintering Temperature on the Densification and Magnetic Performance of NiCuZn-Ferrites (CuO: 0–6 wt.%)

Effect of Bi2O3–CuO Flux on the Microstructure, Soft Magnetic Properties, and Gyromagnetic Properties of NiCuZn Ferrites for LTCC Devices

Enhanced electromagnetic properties of low-temperature sintered NiCuZn ferrites by doping with Bi2O3

Comparison of Magnetic Properties of Low-Temperature-Fired NiCuZn Ferrites under Low- and High-Bi2O3 Doping Modes

Low-Fire NiO-CuO-ZnO Ferrite with Bi2O3

Synergy effects between Li0.42Zn0.27Ti0.11Fe2.2O4 nanoparticles and CuO-Bi2O3 mixtures in low-temperature sintered LiZnTi ferrites with enhanced gyromagnetic and microwave dielectric properties

Synthesis and magnetic properties of low-temperature sintered, LMZBS glass-doped dense NiCuZn ferrites

Structure, Morphology, and Magnetic Properties of High-Performance NiCuZn Ferrite

O 3 ‐ doping controlled magnetic and dielectric properties of low ‐ temperature co ‐ fired NiCuZn ferrite for high ‐ frequency applications

Effects of MgO addition on the DC-bias-superposition characteristic of low-temperature-fired NiCuZn ferrites

Magnetic and dielectric properties of NiCuZn ferrite with optimized Cu content and sintered by a two-step process

Microstructures and magnetic properties of NiCuZn ferrite ceramics doped with MnO2–Bi2O3

Evaluation of the Electromagnetic Characteristics on Ag/NiCuZn Ferrite Sintered Bodies

Influence of Bi2O3-Nb2O5 additive on microstructure and magnetic properties of LiZn ferrites

Microstructure and magnetic properties of Ni–Zn ferrite ceramics with different Ni2+ contents

Magnetic and Electrical Properties of Low-Temperature Sintered Mn-doped NiCuZn Ferrites

Effects of Microstructure on the Temperature Dependence of Relative Initial Permeability of NiCuZn Ferrites