Abstract:With green and low-carbon developments in oil fields, an increasing amount of repaired oil tubing is being used as oil and gas transmission pipelines in China. However, due to differences in manufacturing standards between oil tubing and transmission pipelines, there are inevitably some issues during their use. This paper investigates a case of cracking failure in repaired oil tubing used as a gathering and transportation pipeline. The failure occurred after eight months of operation and was characterized by a circumferential crack at the male thread end of the tubing joint. To determine the root cause of the failure, a series of experiments were conducted on the oil tubing. The experiments included visual inspection, chemical composition analysis, mechanical properties testing, hardness testing, metallographic examination, and microstructure analysis. The results revealed that the thread of the cracked tubing was not tightened to the specified position; the connection between the tubing and the coupling was welded in a circumferential direction; and cracks occurred in the heat-affected zone of the weld. Chemical composition, tensile performance, and the Charpy impact of the tubing meet the requirements of API 5CT for P110 material, and no abnormalities were found in the metallographic structure. The microstructure at the weld toe of the fracture is martensite, and the hardness is 476 HV10. Based on the thermal simulation verification test, when the material of the tubing cools from 1200 °C, which is located in the coarse HAZ temperature zone, the base metal transforms into martensite with a little granular bainite, exhibiting its highest hardness value at 371 HV10, which is higher than the allowable hardness for carbon steel and indicates the material has poor weldability. The reasons for the cracking and failure of the tubing are that the P110 repaired tubing has a high carbon equivalent and poor weldability. During the welding process, martensitic structure was formed at the weld toe, and cold cracks appeared in the heat-affected zone, resulting in failure. To avoid the reoccurrence of such failure, recommendations are proposed.

Establishment Regression Equation Between Welding Parameter and CTOD of X70 Pipeline Tube

Establishment of regression equation between impact ductility and girth joint welding parameter of X70 pipeline steel

Study on TRIP Effect of X65 Pipeline Steel

Thermo-Mechanical Coupling Computation and Warping Analysis During Controlled-Cooling of X65 Heavy Pipeline-Plate

Neural Network Between Impact Ductility of Girth Joint of X70 Pipeline Steel and Welding Parameter

Thermal, metallurgical and mechanical analysis of circumferentially multi-pass welded P92 steel pipes

Pressure reduction strategy based on a new CTOD model considering room temperature creep for X80 pipeline steel

Influence of Welding Residual Stress on the CTOD Design Curve

Carbon diffusion in dissimilar joints between P91 and 12Cr1MoV steels welded by different consumables at high temperature

Evolution of welding residual stresses during cyclic tests in welded tubular joints

3D finite element analysis and optimization of welding residual stress in the girth joints of X80 steel pipeline

Quantitative Correlation between Thermal Cycling and the Microstructures of X100 Pipeline Steel Laser-Welded Joints

Failure Analysis of Cracked P110 Repaired Tubing Used for Gas Transmission

Welding residual stress analysis of the X80 pipeline: simulation and validation

The Development of a Continuous Constitutive Model for Thin-Shell Components with A Sharp Change in the Property at Welded Joints

Fracture analysis of X80 welded joints with variable wall thickness and misalignment

Investigation of the tensile strain response of the girth weld of high-strength steel pipeline

Numerical study on the strain capacity of girth-welded X80 grade pipes

Mechanical Expanding Diameter Process of X70 JCOE Pipe

Cracking Analysis on X80 Steel Oil Pipe during JCOE Forming

Effect of different welding parameters on residual stress and deformation of 20/0Cr18Ni9 dissimilar metal arc-welding joint