Experiment Study of Microstructure Property and Its Control of Submerged Arc Welding Seam of X80 Pipeline Steels

ZHANG Min,YAO Cheng-wu,ZHOU Yong-xin,WANG Wei-bo

DOI: https://doi.org/10.3321/j.issn:1000-5870.2006.05.021

2006-01-01

Abstract:Based on the design of strengthening acicular ferrite using bainite,the Mn-Ni-Mo-Ti-B alloy system submerged-arc welding wire for X80(the yield strength of σ_s≥551 MPa) pipeline steel was fabricated according to the technological route,which is to increase the degree of separation between the bainite transition region and high-temperature ferrite transition region by reducing the content of carbon element,raising the content of Mn element,and adding Ni element.The results of mechanics performance test of weld metal,and microscopic analysis by scanning electron microscope(SEM),transmission electron microscope(TEM),respectively,indicate that excessive content of Mn is disadvantageous to the intragranular nucleated acicular ferrite.The cold cracking sensitivity index(P_(cm)) of weld metal increases with Mn content increasing,the austenite grain of weld metal is thinner when the P_(cm) of weld metal is higher.Thereby,the austenite grain boundaries increases,which is effective for the formation of bainite nucleation and is disadvantageous to the content of acicular ferrite.Ni element has light contributions to P_(cm),and makes the matrix of weld metal apt to alternate slip.Thereby,the adequate content of Ni element is beneficial to the toughness of weld metal.The laths of acicular ferrite nucleated at inclusions grow radially,and the depletion of alloying elements such as Mn and Ti may increase the driving force for ferrite transformation,which will lead to form acicular ferrite preferentially in the region.In addition,there is not depletion of Ni element around the inclusions.