Buliding Ultrathin Li4mn5o12 Shell for Enhancing the Stability of Cobalt-Free Lithium-Rich Manganese Cathode Materials
Yuhong Qiu,Jiaxuan Liao,Xuefeng Peng,Lichun Zhou,Jie Yan,Yaochen Song,Linnan Bi,Xin Long,Liang He,Qingyu Xie,Sizhe Wang
DOI: https://doi.org/10.2139/ssrn.4280762
2022-01-01
SSRN Electronic Journal
Abstract:The lithium-ion battery has the advantages of high energy density, long service life, and good safety performance, and is used as an ideal energy storage device. Cobalt-free lithium-rich manganese cathode materials have attracted much attention due to their high specific capacity and low cost. However, its poor cycling performance is not conducive to practical application. So far, researchers have mainly addressed this problem with surface coatings. In this study, spinel Li4Mn5O12 was successfully prepared by wet chemical method to modify the surface of Li1.2Ni0.2Mn0.6O2. The X-ray diffraction (XRD) and X-ray photoelectron spectroscopy (XPS) test results showed that the crystal structure of the samples did not change significantly, but the cationic order was improved. The results of the scanning electron microscope (SEM), energy dispersive spectrometer (EDS), and transmission electron microscope (TEM) showed that an ultrathin spinel Li4Mn5O12 surface-modified layer with a thickness of about 10 nm was successfully constructed on the raw material surface. In addition, the lithium-ion diffusion coefficients (DLi+) of the raw materials and modified materials were calculated by electrochemical impedance spectroscopy (EIS) test and impedance fitting. The results indicated that the ultrathin Li4Mn5O12 surface modification shell can increase the lithium-ion diffusion rate of the material and improve the rate capability of the material. So, the results show that the surface modification layer of spinel Li4Mn5O12 can reduce the oxygen loss of the first cycle and improve the cationic order of the material. Therefore, the first coulombic efficiency of Li4Mn5O12/Li1.2Ni0.2Mn0.6O2 material at the current density of 12.5 mA×g-1 reaches 80.46%, and the capacity retention rate reaches 91.74% after 50 cycles, which is 3.36% and 21.23% higher than that of the raw materials, respectively. It showed better electrochemical reversibility and cyclic stability. This study provides a straightforward and convenient modification method for improving the stability of cobalt-free lithium-rich manganese cathode materials and has a favorable application prospect.