Cultivating a Comprehensive Understanding of Microstructural Attributes and Wear Mechanisms in FeCrCoNiAlTi x High-Entropy Alloy Coatings on TC6 Substrates Through Laser Cladding Fabrication
Xiangqing Wu,Guanhua Zhou,Dianjun Sun,Lianyang Chen,Jiayu He,Shaoqing Wang,Faqin Xie
DOI: https://doi.org/10.1016/j.jallcom.2024.173865
IF: 6.2
2024-02-17
Journal of Alloys and Compounds
Abstract:Titanium effectively improves the hardness of FeCrCoNiAl high-entropy alloy (HEA) coatings. In this study, FeCrCoNiAlTi x (x = 0, 0.3, 0.5, 0.8, and 1.0) high-entropy alloy coatings were successfully prepared on TC6 titanium alloy substrates via laser cladding(LC). Through the preparation of LC, the effects on the microstructure, phase composition and fretting wear behavior of coatings with different Ti molar ratios were investigated in detail. The results showed that the FeCrCoNiAlTi x (x = 0, 0.3) HEA coatings consisted of face-centered cubic (FCC) and body-centered cubic (BCC) phases. With increasing Ti content of the FeCrCoNiAlTi x (x = 0.5, 0.8, and 1.0) HEA coatings, a new eutectic BCC2 hard phase appeared. The FCC phase was the continuous in the microstructure, whereas the BCC and BCC2 phases formed a hard skeleton. The hardness of the FeCrCoNiAlTi x HEA coatings increased with increasing Ti content, and the hardness of the Ti1.0 HEA coating reached a maximum of 848 HV 0.1 . The FeCrCoNiAlTi x (x = 0,0.3,0.5,0.8, and 1.0) HEA coatings effectively improved the resistance of TC6 alloys to fretting by fatigue, oxidative, adhesive, and abrasive wear.
materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering