Omega phase formation and deformation mechanism in heat treated Ti-5553 alloy under high strain rate compression

Tayyeb Ali,Lin Wang,Xingwang Cheng,Anjin Liu,Xuefeng Xu

DOI: https://doi.org/10.1016/j.matlet.2018.10.057

IF: 3

2019-01-01

Materials Letters

Abstract:•Heat treated Ti-5553 without aging, under high strain rate compression.•Deformation through slipping and twining.•Omega phase nucleation in beta phase after superimposed compression.

What problem does this paper attempt to address?

In-situ Investigation Via High Energy X-ray Diffraction of Stress-Induced(0002)α→(110)β Transformation in a Ti-5.5Mo-7.2Al-4.5Zr-2.6Sn-2.1Cr Alloy

Duoduo Wang,Qunbo Fan,Ran Shi,Yu Zhang,Haichao Gong,Liang Wang,Yunfei Xue,Yang Ren

DOI: https://doi.org/10.1016/j.msea.2020.139154

2020-01-01

Abstract:The deformation and load partitioning mechanisms among phases are critical to the detailed understanding of heterogeneous stress distributions at the submicron scale during the process of elastic-plastic transformation in dual-phase (α+β) titanium alloys. Therefore, in this work, a Ti-5.5Mo-7.2Al-4.5Zr-2.6Sn-2.1Cr titanium alloy was investigated via in-situ high energy X-ray diffraction. We examined the evolution of the lattice strain, peak intensity, and full width at half maximum under uniaxial tensile loading at room temperature. The results indicated that the stress-induced (0002)α→(110)β transformation can be preferentially initiated for lattice strains of 702 × 10−6–1500 × 10−6 and 592 × 10−6–1355 × 10−6 during the elastic loading stage of the {0002}α and {110}β reflections, respectively. In addition, various dog-bone-shaped specimens with interrupted strain amplitudes (0.3%, 3%, 5% and 8.5%) were characterized via transmission electron microscopy. The corresponding selected area electron diffraction pattern confirmed the occurrence of a (0002)α//(110)β Burgers orientation relationship when the alloy was subjected to a strain of ε = 0.3%. Furthermore, the results revealed that the anisotropic non-linear response of specific reflections (i.e., the (0002)α and (110)β reflections) will cause a phase transformation.
Mechanical Properties and Deformation Mechanisms in Microscale Ti-55531 Alloy

Kou Wenjuan,Sun Qiaoyan,Xiao Lin,Sun Jun

DOI: https://doi.org/10.1051/matecconf/202032111024

2020-01-01

MATEC Web of Conferences

Abstract:The mechanical behaviors and deformation mechanisms of solution treated and 450°C aged Ti-55531 alloy microsamples are investigated by the micro-compression and micro-bending. The results show that the dislocation slip is a concentrated movement in the solution treated microsamples which containing nanoscale ω phase. Under the tensile and compressive stress, there were serious strain bursts occurred in the plastic deformation of solution treated microsamples. But the dislocation slip is transmit at the phase interface in the 450°C aged microsamples which containing high density of α phase. The deformation behavior exhibits high strength and excellent stability in the micro-compression and micro-bending process. The different mechanical behaviors and deformation mechanisms of Ti-55531 alloy containing different second phase have significant guidance for tailoring the microstructure and mechanical properties. Key words: Titanium, Micro-compression, Micro-bending, Dislocation, Mechanical behavior
Characterization of Hot Deformation Microstructure of a Near Beta Titanium Alloy Ti-5553

Ke Hua,Xiangyi Xue,Hongchao Kou,Jiangkun Fan,Bin Tang,Jinshan Li

DOI: https://doi.org/10.1016/j.jallcom.2014.07.056

IF: 6.2

2014-01-01

Journal of Alloys and Compounds

Abstract:The hot deformation microstructures of Ti-5553 titanium alloy in the temperature range of 750-900 degrees C and strain rate range of 10(-3)-10(-1) s(-1) were investigated by hot compressive testing on the Gleeble-3500 thermo-mechanical simulator. Transmission electron microscope (TEM) and electron back scattered diffraction (EBSD) were employed to investigate the effect of deformation conditions on the microstructure and deformation mechanism. The results showed that deformation parameters can significantly affect microstructure evolution, and dynamic recrystallization is more noticeable at temperature 900 degrees C and strain rate 10(-3) s(-1). Hot deformation dramatically increased the fraction of low-angle grains boundaries (LAGBs), and the misorientation distribution skewed toward low-angle rotations, and also changed the strict Burgers-relationship between alpha and beta phase. Furthermore, thermo-mechanical processing can increase the driving force of phase transformation. The phenomenon of alpha phase globularization can be explained accurately by beta phase wedges model. (C) 2014 Elsevier B.V. All rights reserved.
Hot Deformation Behavior of a Novel Near-β Titanium Alloy Ti-5.5Mo-6V-7Cr-4Al-2Sn-1Fe in (α+β) Phase Region

Jinyang Gai,Jun Cheng,Jinshan Li,Zhaoxin Du,Wen Zhang,Sen Yu,Zhentao Yu

DOI: https://doi.org/10.3389/fmats.2019.00343

2020-01-14

Frontiers in Materials

Abstract:The hot deformation behavior of a novel near-beta titanium alloy Ti-5.5Mo-6V-7Cr-4Al-2Sn-1Fe in (α+β) phase region in the temperature of 605~755°C and strain rate range of 10−3~10−1/s−1 was investigated on the Gleeble-3800 thermo-mechanical simulator. The results showed that the deformation parameters can have a significant influence on flow softening behavior and the microstructure evolution, as well as dynamic recrystallization is remarkable at temperature 755°C and strain rate 10−3s−1. The flow stress decreases with the increase of temperature and decrease of strain rate. With the rise of temperature and strain rate, the content of α phase gradually decreases. During the thermal deformation process, the α phase content decreases with the increase of the strain rate and the size of α phase decreases with increasing temperature. αGB is short rod or spherical. And α phase precipitated after short-term aging preferentially nucleated within the grains after aging treatment. Moreover, the thermal-mechanical process does not induce α phase generation compared to general heat treatment.

materials science, multidisciplinary
Microstructural Variation and a Physical Mechanism Model for a Ti-55511 Alloy during Double-Stage Hot Deformation with Stepped Strain Rates in the β Region

Dao-Guang He,Gang Su,Yong-Cheng Lin,Yu-Qiang Jiang,Zhou Li,Zi-Jian Chen,Xin-Tao Yan,Yu-Chi Xia,Yang-Chen Xie

DOI: https://doi.org/10.3390/ma14216371

IF: 3.4

2021-10-25

Materials

Abstract:The microstructural variation and high-temperature flow features of a Ti-55511 alloy in the β region are studied by utilizing double-stage compression with a stepped strain rate. The results demonstrate that the stresses in the latter stage of hot compression markedly reduce as the strain at the previous stage or the strain rate at the previous/latter stage drops. Moreover, the annihilation/interaction of substructures is promoted, and the distinct refinement of the dynamic recrystallization (DRX) in the β grain can be found. However, the coarsening of the β grain and the consumption of dislocation substructures are accelerated at high temperatures. Furthermore, the principal DRX nucleation mechanism of the Ti-55511 alloy during double-stage compression with a stepped strain rate in the β region is discontinuous DRX. Additionally, by using the microstructural variation characteristics related to the forming parameters, a physical mechanism equation is modeled to forecast the forming features, the DRX fraction, and the size of the β grain in the investigated alloy. The forecasted results are in accordance with the tested results, indicating that the established model can accurately forecast the microstructure variation and flow features of the studied alloy.

materials science, multidisciplinary,chemistry, physical,physics, applied, condensed matter,metallurgy & metallurgical engineering
Investigation on the thermal deformation mechanisms and constitutive model of Ti-55511 titanium alloy

Xintong Wang,Pengwei Liu,Chuangxiong Liang,Tonggang Lu,Tianyi Feng,Haozhe Niu,Yue Dong,Xingang Liu

DOI: https://doi.org/10.1016/j.jmrt.2024.11.057

IF: 6.267

2024-11-10

Journal of Materials Research and Technology

Abstract:This study presents a comprehensive analysis of the hot deformation behavior of the Ti-55511 alloy over a temperature range of 700 °C to 950 °C and strain rates from 0.001 s− 1 to 1 s− 1 , utilizing isothermal compression testing alongside electron backscatter diffraction (EBSD) and transmission electron microscopy (TEM). The investigation focuses on the influence of various hot deformation parameters on the microstructural evolution of distinct phase regions within the alloy. At higher strain rates (0.1 s− 1 to 1 s− 1 ), the primary softening mechanisms for β grains in the α+β two-phase region are identified as continuous dynamic recrystallization (CDRX) and dynamic recovery (DRV), while in the β single-phase region, discontinuous dynamic recrystallization (DDRX) and DRV predominate. Conversely, at lower strain rates (0.001 s− 1 to 0.01 s− 1 ), the softening of β grains in the two-phase region is primarily governed by DRV, whereas in the single-phase region, DDRX and CDRX are the dominant mechanisms. Additionally, based on stress-strain data corrected for friction and temperature effects, an elastoplastic constitutive model is developed, incorporating strain rate and temperature to predict peak stress in the two-phase regions of the Ti-55511 alloy. This examination of the thermal deformation behavior and microstructural evolution of the Ti-55511 alloy provides significant theoretical and practical insights for optimizing the manufacturing processes of aviation die forging, tailoring microstructures, and enhancing hot working techniques.

materials science, multidisciplinary,metallurgy & metallurgical engineering
Study on Hot Deformation Behavior and Microstructure Evolution of Ti-55 High-Temperature Titanium Alloy

Fengyong Wu,Wenchen Xu,Xueze Jin,Xunmao Zhong,Xingjie Wan,Debin Shan,Bin Guo

DOI: https://doi.org/10.3390/met7080319

IF: 2.695

2017-01-01

Metals

Abstract:The isothermal compression experiment of as-rolled Ti55 alloy was carried out on a Gleeble-3800 thermal simulation test machine at the deformation temperature range of 700–1050 °C and strain rate range of 0.001–1 s−1. The hot deformation behavior and the microstructure evolution were analyzed during thermal compression. The results show that the apparent activation energy Q in α+β dual-phase region and β single-phase region were calculated to be 453.00 KJ/mol and 279.88 KJ/mol, respectively. The deformation softening mechanism was mainly controlled by dynamic recrystallization of α phase and dynamic recovery of β phase. Discontinuous yielding behavior mainly occurred in β phase region, which weakened gradually with the increase of deformation temperature (>990 °C) and strain rate (0.01–1 s−1) in β phase region. The processing map derived from Murty’s criterion was more accurate in predicting the hot workability than that derived from Prasad’s criterion. The optimized hot working window was 850–975°C/0.001–1 s−1, in which sufficient dynamic recrystallization occurred and α + β-transus microstructure was obtained. When deformed at higher temperature (≥1000 °C), coarsened lath-shape β-transus microstructure was formed, while deformed at lower temperature (≤825 °C) and higher strain rate (≥0.1 s−1), the dynamic recrystallization was not sufficient, thus flow instability appeared because of shear cracking.
Microstructure Evolution of a Ti–Al–Sn–Zr Based Alloy During the Hot Compression Deformation

Liyuan Sheng,Yang,Chen Lai,Xin Chen,Tingfei Xi

DOI: https://doi.org/10.1166/mex.2019.1599

2019-01-01

Materials Express

Abstract:The Ti–Al–Sn–Zr based alloy was fabricated and its deformation behavior was investigated with increasing of temperature and strain rate. Microstructure and phase of the as-fabricated, heat treated and deformed alloy was characterized by OM, XRD and TEM. The results exhibited that the addition of Mo, Nb and Ta promoted the precipitate of β phase at relative low heat treatment temperature. And the β phase has relative good phase interface with the αphase. During the compression test, the compressive strength of the alloy dropped with the strain rate decreasing and the testing temperature rising. When the compression deformation was preformed above α phase transformation temperature, the high strain rate would promote the phase transformation. When the alloy was compressed with strain rate of 1 s–1, it almost had the similar compressive strengths at 960 °C and 940 °C. Moreover, the same phenomenon appeared when the compression was carried out at 960 °C and 980 °C with stain rate of 0.01 s–1. Such a phenomenon should be ascribed to the existence of high amount of β phase which could contribute to the strength.
Deformation Behaviour and Microstructural Evolution During the Hot Compression of Ti-5Al4Zr8Mo7V Alloy

Jia Lei,Wenguang Zhu,Lei Chen,Qiaoyan Sun,Lin Xiao,Jun Sun

DOI: https://doi.org/10.1016/j.mtcomm.2019.100873

IF: 3.8

2020-01-01

Materials Today Communications

Abstract:The hot deformation behaviour and microstructural evolution of a metastable beta titanium alloy Ti-5Al4Zr8Mo7V at deformation temperatures of 775, 795, 815 and 835. with true strains of 0.25, 0.50 and 1.00 over a strain rate range of 0.001-1 s(-1) were investigated to optimize the hot working process window. An Arrhenius type constitutive equation is obtained to describe the hot deformation characteristics. The flow stress behaviour and the deformation thermal activation energy of 187 kJ/mol indicate dynamic recovery of the alloy. Based on the hot compression data, the processing maps at strains of 0.25, 0.50 and 1.00 are constructed to characterize the hot workability. Microstructural investigation confirms the occurrence of flow localization at the predicted unstable region. Whereas, globularization of a phase, dynamic recovery and dynamic recrystallization of beta phase are the main dynamic softening mechanisms. The results show that the hot workability of Ti-5Al4Zr8Mo7V alloy is better at higher deformation temperature, higher strain, and lower strain rate, in which case the original microstructure is replaced by the equiaxed a phase and recrystallized beta phase.
High-temperature tensile deformation behavior and microstructure evolution of Ti55 titanium alloy

Zhangguang Liu,Peijie Li,Liangtong Xiong,Taiying Liu,Liangju He

DOI: https://doi.org/10.1016/j.msea.2016.10.095

2017-01-01

Abstract:High temperature tensile and electron backscatter diffraction (EBSD) techniques were combined to perform a systematic investigation for the hot deformation behavior and microstructure evolution of the Ti55 alloy. Under temperatures ranging from 885 to 935°C and stain rates of 8.3×10−4 s−1−1.33×10−2 s−1, all the flow curves of the Ti55 alloy exhibit similar behaviors: after reaching the peak flow stress, the curves enter into a softening stage and then remain a steady level, where the maximum superplastic elongation of 987% indicates good superplasticity. Detailed microstructure characterizations under different deformation stages show that the grain aspect ratios decrease greatly and the fractions of high angle boundaries (>15°) increase rapidly at the softening stage. These observations are attributed to the dynamic recrystallization, in which low angle grain boundaries (<5°) evolve into high angle boundaries and the formation of equiaxed grains is accelerated. In contrast, no obvious changes in either the grain aspect ratios or the fractions of high angle boundaries occur at the steady flow stage, while the initial texture gradually disappears and the Schmid factor increases with the further straining. At this stage, the deformation mechanism is grain boundary sliding and grain rotation would accommodate the process of grain boundary sliding. Moreover, the main softening mode responsible for the flow behaviors has been identified as discontinuous dynamic recrystallization, which completely neutralized the effect of work hardening at the quasi stable deformation stage.
Hot Workability and Microstructural Evolution of Ti-5.5Al-5Mo-5V-2Nb-1Fe-1Zr Titanium Alloy Based on the Different Phase Zones during Plastic Deformation at High Temperatures

Yushe Gao,Xianghong Liu,Haisheng Chen,Xiangyi Xue,Huixian Gao,Wenzhong Luo,Kaixuan Wang,Shaoqiang Li,Yuxuan Du

DOI: https://doi.org/10.3390/met13010092

IF: 2.695

2023-01-02

Metals

Abstract:Hot workability and microstructural evolution of Ti-5.5Al-5Mo-5V-2Nb-1Fe-1Zr titanium alloy, which is also called Ti555211 titanium alloy, are investigated during compressive deformation at different temperatures and strain rates. It can be found that Ti555211 samples deformed at 750 and 850 °C comprised α and β phases, while Ti555211 samples deformed at 950 and 1050 °C consist of single β phase. When Ti555211 sample undergoes compressive deformation in the α + β phase region, microstructures of β phase vary more substantially than those of α phase, which means that plastic deformation of Ti555211 sample is governed by β phase. The process parameters are optimized by establishing processing maps based on dynamic material model. Ti555211 alloy generally possesses the better hot workability in the β phase zone. In the β phase zone of Ti555211 alloy, the best hot process area involves temperature range from 925 to 1025 °C and a strain rate range of 0.005 to 0.03 s−1.

materials science, multidisciplinary,metallurgy & metallurgical engineering
Superplastic Deformation and Microstructure Evolution of Ti-55 Alloy Sheet

Liu Zhangguang,Li Jianhui,Li Peijie,Gao Haitao,Xiong Liangtong

DOI: https://doi.org/10.13373/j.cnki.cjrm.XY16090005

2017-01-01

Abstract:The superplastic deformation and microstructure evolution at different temperatures ( 885 ~935 ℃) and strain rates (8.30 ×10 -4 ~1.32 ×10 -2 s-1 ) were investigated.The results showed that the fine-grained Ti-55 alloy sheet exhibited good super-plastic deformation performance.The maximum elongation of 987%could be achieved at 925℃and 6.64 ×10 -3 s-1 , and the high e-longation of 872%could be obtained at a high strain rate of 1.32 ×10 -2 s-1 .At the same strain rate, with the increasing deformation temperature, the extent of dynamic recrystallization increased and the volume fraction of αphase decreased, which promoted αphase transformation.Meanwhile, the primaryαphase grains could be refined.At the same superplastic tension temperature, the primaryαphase grains could coarsen and the content ofβphase increased with the strain rate decreasing.Additionally, the coarsening degree ofαphase grains in the deformed gauge became more serious than that in the undeformed grip.The content ofαphase decreased with the increase of deformation degree.The deformation of Ti-55 alloy material could accelerate the coarsening rate ofαphase grains and pro-moteαto βphase transformation.
Investigation of High-Temperature Constitutive Behavior of Ti555211 Titanium Alloy Subjected to Plastic Deformation in the Different Phase Regions

Yushe Gao,Xiangyi Xue,Huixian Gao,Wenzhong Luo,Kaixuan Wang,Shaoqiang Li,Xianghong Liu,Yuxuan Du

DOI: https://doi.org/10.3390/met12101562

IF: 2.695

2022-09-22

Metals

Abstract:Ti555211 titanium alloy is subjected to plastic deformation in the dual-phase (α + β phase) zone and single-phase (β phase) zone at various deformation temperatures and strain rates. High-temperature constitutive equations of the alloy in the dual-phase zone and single-phase zone are established in order to describe deformation behavior of the alloy in the different phase zones. By comparing the constitutive equation of the alloy in the dual-phase zone with that of the alloy in the single-phase zone, the deformation activation energy of the former was found to be higher than that of the latter. It is obvious that the deformation activation energy of α phase is obviously greater than that of β phase. Furthermore, the microstructural evolution of the alloy is different in the dual-phase zone and single-phase zone. When the alloy was subjected to plastic deformation in the dual-phase zone, the size of the grains in the β phase increased with the decreasing strain rate. When the alloy was subjected to plastic deformation in the single-phase zone, the size of the grains in the β phase considerably increased with the increasing deformation temperature. In particular, in the microstructures of the alloy subjected to plastic deformation in the single-phase region, the elongated grains can be observed at higher strain rates. Furthermore, it is more difficult for the alloy to induce plastic deformation in the dual-phase region than in the single-phase region.

materials science, multidisciplinary,metallurgy & metallurgical engineering
Influence of cooling rate on phase precipitation and deformation mechanism of a novel metastable titanium alloy

Kaige Wang,Di Wu,Dong Wang,Zixuan Deng,Yueyan Tian,Ligang Zhang,Libin Liu

DOI: https://doi.org/10.1016/j.msea.2021.142151

2022-01-01

Abstract:This work investigated the effect of cooling rate (water quenching and air cooling) on the precipitation of omega phase after solution treatment in beta-phase region, and its effect on the mechanical properties in a novel metastable beta titanium alloy (Ti-5Mo-3Cr-Fe-3Zr). The initial microstructures, phase composition and deformation-induced microstructures have been investigated using SEM, EBSD, XRD, and TEM. The phase composition of water-quenched alloy and air-cooled alloy are beta, alpha '', and omega phase. The size and volume fraction of omega phase of air-cooled alloy are larger than that of water-quenched alloy, resulting in an increase in tensile strength and a decrease in ductility. Deformation mechanisms of Ti-5Mo-3Cr-Fe-3Zr alloy with different cooling rate change from stress-induced omega phase transformation and dislocation slip to only dislocation slip. The stress-induced omega lamellas parallel to [1-11](beta) direction along the [0001](omega 1) direction, which is formed by {112}(beta)< 111 >(beta) slip. Dislocations can cut through the encountered omega phase to form omega-free deformation bands, which accounts for the ductility.
A dislocation density-based model and processing maps of Ti-55511 alloy with bimodal microstructures during hot compression in α+β region

Yi-Wei Xiao,Y.C. Lin,Yu-Qiang Jiang,Xiao-Yong Zhang,Guo-Dong Pang,Dan Wang,Ke-Chao Zhou

DOI: https://doi.org/10.1016/j.msea.2020.139692

2020-07-01

Abstract:Hot compression features of Ti-55511 alloy are investigated by high-temperature compression tests in α+β region. It is found that the flow stress and softening mechanisms are obviously influenced by deformation conditions. The true stress decreases with the reduced strain rate or the raised temperature. Furthermore, dynamic recrystallization easily occurs at low temperatures, while dynamic recovery (DRV) mainly occurs at high temperatures. A dislocation density-based constitutive model, which is associated with DRV, work hardening mechanisms and the spheroidization of α phases, is established and validated to describe flow behavior. The correlation coefficient (R) and average absolute relative error (AARE) of the established model are 0.9924 and 6.8%, respectively. 3D power dissipation efficiency maps and processing maps are established to determine the appropriate processing window, i.e., too low temperatures (lower than 973 K) or too high strain rates (higher than 1 s−1) easily induce flow instability. Therefore, the medium temperature (1003–1063 K) and the low strain rate (0.001–0.1 s−1) are applicable for thermal compression of the studied titanium alloy.
High-temperature deformation behavior and recrystallization mechanism of a near beta titanium alloy Ti-55511 in β phase region

Shuangxi Shi,Jinyang Ge,Y.C. Lin,Xiaoyong Zhang,Kechao Zhou

DOI: https://doi.org/10.1016/j.msea.2022.143335

2022-05-26

Abstract:Isothermal compression tests, electron backscatter diffraction (EBSD) observations and quantitative analysis were performed to investigate high-temperature deformation behavior and recrystallization mechanism of Ti-55511 alloy in β phase region. The stress-strain curves, calculated activation energy and microstructure characterization show that dynamic recovery (DRV) and dynamic recrystallization (DRX) are the main soften mechanisms. DRX becomes more significant with decreasing strain rate and increasing deformation temperature and true strain. Recrystallization grains are identified by calculated grain orientation spread (GOS). It is found that quantitative microstructural characteristics, such as DRX volume fraction and DRX grain size, are strongly dependent on process parameters. The discontinuous dynamic recrystallization (DDRX) by grain boundaries bulging and continuous dynamic recrystallization (CDRX) by progressive sub-grains rotation are observed in the deformed microstructure of Ti55511 alloy. The flow softening rate and kinetics exponent of DDRX are higher than those of CDRX. With increasing deformation temperature, DRX mechanism has transformed from DDRX to CDRX, resulting in the unexpected decrease of DRX kinetics exponent n D and flow softening rate. The h bcc fiber, ε bcc fiber and x bcc fiber are the dominant texture component in deformed Ti–55511 alloy. The weakening of the deformation texture is accompanied by the occurrence of DRX, which can be attributed to the random orientation distribution of DRX grains.
Plastic deformation mode and / slip transfer of Ti-5Al-2.5Cr-0.5Fe-4.5Mo-1Sn-2Zr-3Zn titanium alloy at room temperature

Xin Liu,Yan Qian,Qunbo Fan,Yu Zhou,Xinjie Zhu,Duoduo Wang

DOI: https://doi.org/10.1016/j.jallcom.2020.154209

IF: 6.2

2020-01-01

Journal of Alloys and Compounds

Abstract:The plastic deformation mode and slip transfer between the alpha and beta phases of Ti-5Al-2.5Cr-0.5Fe-4.5Mo-1Sn-2Zr-3Zn titanium alloy were investigated using a combination of ex-situ scanning electron microscopy tensile tests and electron backscatter diffraction characterization. With increasing tensile strain, local orientation changes (which lead to the sub-grain boundary generation and migration) occurred in the alpha phase, resulting in grain subdivision/coalescence. Afterward, the elongated alpha grains were sub-divided (in general) into small equiaxed grains. Abrupt changes in the crystal orientation of the continuous beta-matrix were, however, rare. Three primary slip systems (prismatic and basal slip: alpha phase and {110}< 111 > slip: beta phase) accounted for more than 70% of the total slip system activity at each strain level. These systems could be activated with very low Schmid factors (<0.1) at high strains. The compatible deformation between the alpha and beta phases was realized mainly through the slip transfer correlated with the three primary slip systems, and the prismatic slip system was the most active system. In general, the alpha phase underwent plastic deformation first and compelled plastic deformation of the separated beta grains. Subsequently, the deformed beta grains transmitted the strain between an adjacent alpha grain and other alpha grains, leading to deviations from the uniaxial stress state in the local region. This resulted in wide distributions of the activated slip systems with various Schmid factors, and considerable strain concentration and failure in the alpha phase near the phase boundaries. (C) 2020 Elsevier B.V. All rights reserved.
Microstructure evolution and a unified constitutive model for a Ti-55511 alloy deformed in β region

Yu-Qiang Jiang,Y.C. Lin,Guan-Qiang Wang,Guo-Dong Pang,Ming-Song Chen,Zhi-Chao Huang

DOI: https://doi.org/10.1016/j.jallcom.2021.159534

IF: 6.2

2021-07-01

Journal of Alloys and Compounds

Abstract:The microstructure evolution of a Ti-55511 alloy deformed at high temperatures (from 1163 K to 1253 K) and wide strain rate range (from 10 s−1 to 0.001 s−1) is studied by isothermal compression tests. Based on the sensitivity of dislocation density to deformation conditions, a unified constitutive equation is established to describe the evolution of flow stress, grain size and dynamic recrystallization (DRX) fraction. The results show that the initial grain boundaries are serrated, and the sub-grains and DRX grains are formed with the further deformation. Furthermore, the discontinuous and geometric DRX mechanisms are dominant recrystallization mechanism. Increasing the deformation temperature can increase the DRX fraction and sub-grain size. However, the abnormal growth of β grains occurs at 1253 K. The DRX fraction decreases with the increased strain rate. Meanwhile, the chain-like small DRX grains and the flow localization occur at high strain rates. Also, the established constitutive model is verified by the experimental results, and the correlation coefficient is 0.9929, indicating the excellent prediction ability of the established constitutive model.

materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering
Spheroidization and dynamic recrystallization mechanisms of Ti-55511 alloy with bimodal microstructures during hot compression in α+β region

Y.C. Lin,Yi-Wei Xiao,Yu-Qiang Jiang,Guo-Dong Pang,Hong-Bin Li,Xiao-Yong Zhang,Ke-Chao Zhou

DOI: https://doi.org/10.1016/j.msea.2020.139282

2020-04-01

Abstract:Spheroidization and dynamic recrystallization (DRX) mechanisms of a Ti-55511 alloy during hot compression in α+β region is investigated. It is found that the spheroidization of lamellar α phases and DRX of β phases, which are obviously influenced by deformation conditions, are the main softening mechanisms. The spheroidization fraction of lamellar α phases first increases with the raised temperature or strain rate. However, the spheroidization fraction of lamellar α phases begins to drop at about 700 °C as the strain rate is higher than 0.01 s−1, and the maximum spheroidization fraction of lamellar α phase is about 2.3%. This phenomenon is attributed to the Implanting-Mechanism, which is induced by the common or close orientation relationships of the spheroidized and equiaxed α phases, as well as few dislocations between the spheroidized and equiaxed α phases. Contrarily, the lamellar α phases are obstructed from equiaxed α phases by a mass of dislocations. Additionally, the DRX degree of β phases increases with the reduced temperature or the raised strain rate.

materials science, multidisciplinary,nanoscience & nanotechnology,metallurgy & metallurgical engineering
Deformation mechanism diagram and deformation instability of a Ti-5Al-5Mo-5V-1Cr-1Fe titanium alloy during the hot compression

Yechen Deng,Yixin An,Yangzhihong Xiao,Xiaodong Zhan,Xiaoyong Zhang,Bingfeng Wang

DOI: https://doi.org/10.1016/j.jallcom.2023.171446

IF: 6.2

2023-07-30

Journal of Alloys and Compounds

Abstract:Controlling the hot deformation mechanism of the titanium alloy and avoiding deformation instability are the key points in the hot forging of the titanium alloy. A high throughput experimental method was used to establish a deformation mechanism map efficiently. A continuously varying strain distribution from 0.3 to 1.4 was obtained by the deformation of the double-cone specimens. At the temperature of 910 °C and the strain rate of 1.37 s −1 , Combining the analysis of metallography and strain-stress curves, the deformation mechanisms in different regions of the double-cone specimens were divided. Dynamic recovery (DRV) and dynamic recrystallization (DRX) work together in the low strain region (<0.62), and DRX gradually becomes the dominant deformation mechanism in the medium strain region (0.62–1.02). In the large strain region (1.02–1.4), amounts of deformation bands (DBs) formed. Electron back scatter diffraction (EBSD) technique was used for the microstructure observation and the analysis of deformation mechanism. The results demonstrate that with an increase in strain, the recrystallization fraction increased from 83.8% to 96.3%. Combining the several results of the double-cone specimens, the hot deformation mechanism diagram with a temperature range of 850–930 °C, and a strain range of 0.3–1.4 was established. When the strain reaches a certain degree, it is difficult to further form new recrystallized grains at the grain boundaries. The formation of recrystallized grains within the deformation band has been characterized using transmission electron microscopy (TEM). Under the action of shear force, fine recrystallized grains form within the elongated grains. The concentrated fine recrystallized grains aggravate the microstructural nonuniformity of the Ti-55511 titanium alloy in this area, which finally leads to the deformation instability.

materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering

Omega phase formation and deformation mechanism in heat treated Ti-5553 alloy under high strain rate compression

In-situ Investigation Via High Energy X-ray Diffraction of Stress-Induced(0002)α→(110)β Transformation in a Ti-5.5Mo-7.2Al-4.5Zr-2.6Sn-2.1Cr Alloy

Mechanical Properties and Deformation Mechanisms in Microscale Ti-55531 Alloy

Characterization of Hot Deformation Microstructure of a Near Beta Titanium Alloy Ti-5553

Hot Deformation Behavior of a Novel Near-β Titanium Alloy Ti-5.5Mo-6V-7Cr-4Al-2Sn-1Fe in (α+β) Phase Region

Microstructural Variation and a Physical Mechanism Model for a Ti-55511 Alloy during Double-Stage Hot Deformation with Stepped Strain Rates in the β Region

Investigation on the thermal deformation mechanisms and constitutive model of Ti-55511 titanium alloy

Study on Hot Deformation Behavior and Microstructure Evolution of Ti-55 High-Temperature Titanium Alloy

Microstructure Evolution of a Ti–Al–Sn–Zr Based Alloy During the Hot Compression Deformation

Deformation Behaviour and Microstructural Evolution During the Hot Compression of Ti-5Al4Zr8Mo7V Alloy

High-temperature tensile deformation behavior and microstructure evolution of Ti55 titanium alloy

Hot Workability and Microstructural Evolution of Ti-5.5Al-5Mo-5V-2Nb-1Fe-1Zr Titanium Alloy Based on the Different Phase Zones during Plastic Deformation at High Temperatures

Superplastic Deformation and Microstructure Evolution of Ti-55 Alloy Sheet

Investigation of High-Temperature Constitutive Behavior of Ti555211 Titanium Alloy Subjected to Plastic Deformation in the Different Phase Regions

Influence of cooling rate on phase precipitation and deformation mechanism of a novel metastable titanium alloy

A dislocation density-based model and processing maps of Ti-55511 alloy with bimodal microstructures during hot compression in α+β region

High-temperature deformation behavior and recrystallization mechanism of a near beta titanium alloy Ti-55511 in β phase region

Plastic deformation mode and / slip transfer of Ti-5Al-2.5Cr-0.5Fe-4.5Mo-1Sn-2Zr-3Zn titanium alloy at room temperature

Microstructure evolution and a unified constitutive model for a Ti-55511 alloy deformed in β region

Spheroidization and dynamic recrystallization mechanisms of Ti-55511 alloy with bimodal microstructures during hot compression in α+β region

Deformation mechanism diagram and deformation instability of a Ti-5Al-5Mo-5V-1Cr-1Fe titanium alloy during the hot compression