Plastic deformation mode and / slip transfer of Ti-5Al-2.5Cr-0.5Fe-4.5Mo-1Sn-2Zr-3Zn titanium alloy at room temperature

Xin Liu,Yan Qian,Qunbo Fan,Yu Zhou,Xinjie Zhu,Duoduo Wang

DOI: https://doi.org/10.1016/j.jallcom.2020.154209

IF: 6.2

2020-01-01

Journal of Alloys and Compounds

Abstract:The plastic deformation mode and slip transfer between the alpha and beta phases of Ti-5Al-2.5Cr-0.5Fe-4.5Mo-1Sn-2Zr-3Zn titanium alloy were investigated using a combination of ex-situ scanning electron microscopy tensile tests and electron backscatter diffraction characterization. With increasing tensile strain, local orientation changes (which lead to the sub-grain boundary generation and migration) occurred in the alpha phase, resulting in grain subdivision/coalescence. Afterward, the elongated alpha grains were sub-divided (in general) into small equiaxed grains. Abrupt changes in the crystal orientation of the continuous beta-matrix were, however, rare. Three primary slip systems (prismatic and basal slip: alpha phase and {110}< 111 > slip: beta phase) accounted for more than 70% of the total slip system activity at each strain level. These systems could be activated with very low Schmid factors (<0.1) at high strains. The compatible deformation between the alpha and beta phases was realized mainly through the slip transfer correlated with the three primary slip systems, and the prismatic slip system was the most active system. In general, the alpha phase underwent plastic deformation first and compelled plastic deformation of the separated beta grains. Subsequently, the deformed beta grains transmitted the strain between an adjacent alpha grain and other alpha grains, leading to deviations from the uniaxial stress state in the local region. This resulted in wide distributions of the activated slip systems with various Schmid factors, and considerable strain concentration and failure in the alpha phase near the phase boundaries. (C) 2020 Elsevier B.V. All rights reserved.