Micromechanical Behaviour of TA15 Alloy Cylindrical Parts Processed by Multi-Pass Flow Forming

X. X. Wang,M. Zhan,P. F. Gao,H. R. Zhang

DOI: https://doi.org/10.1016/j.msea.2018.09.062

2018-01-01

Abstract:Analysis of the micromechanical behaviour of titanium alloys is of fundamental importance to microstructure control and property tailoring of titanium components. In this study, the dependence of deformation history on the micromechanical properties of TA15 titanium spun cylindrical parts processed by the multi-pass flow forming were analysed together with the microstructural features. The results indicate that the indentation hardness of primary α grains (αp) and the transformed β matrix (βt) both increase with the increase of the flow forming strain. The indentation hardness of αp is higher than that of βt, which partly results from the obvious indentation size effect (ISE) of αp. With the increase of the flow forming strain, numerous substructures are generated in this process, which increases the proportion of statistically stored dislocations during indentation tests and thus weakens the influence of the ISE on the indentation hardness. The Young's modulus of αp increases rapidly with deformation, whereas it decreases with the increase of the indenter load. This decrease is attributed to the damage accumulating at higher indentation loads. For βt, there is a minor fluctuation of the Young's modulus with strain variation. After the ISE of αp is eliminated, effect significance of each microstructural feature on the integrated hardness decreases in the order of αp, βt, and the grain interfaces of αp/βt. Meanwhile, with the increase of the flow forming strain, the hardness contribution of αp to the integrated hardness decreases, while those of βt and αp/βt interfaces increase. These findings provide a basis for tailoring desirable properties of TA15 cylindrical parts in the multi-pass flow forming process.