Microstructural and interfacial characteristics of supersonic reclaimed 2024Al-T3 substrate using cold sprayed 2024Al deposit
Yuan Zhong,Zhihao Liu,Yingpeng Zhang,Limei Cha,Chidambaram Seshadri Ramachandran,Qun Wang
DOI: https://doi.org/10.1016/j.matchar.2024.114158
IF: 4.537
2024-07-18
Materials Characterization
Abstract:For a deeper understanding of the cold-sprayed aluminum alloy as well as coating/substrate bonding and splat/splat adhesion mechanisms, X-ray diffraction (XRD), Scanning Electron Microscope (SEM) and Transmission Electron Microscope (TEM) were employed to systematically investigate the phase composition, microstructure and interfacial characteristics of cold sprayed (CS) 2024Al coating on 2024Al-T3 substrate. Within the internal structure of the layer, recrystallization processes induced by intense stress were seen, resulting in the formation of nanograins with sizes ranging from 30 to 100 nm, as well as ultrafine grains with sizes ranging from 100 to 300 nm. The bonding modes of the splat/splat and coating/substrate interface include mechanical bonding and metallurgical bonding; mechanical interlocking was seen as a special mechanical bonding method to enhance the adhesion strength between coating and substrate. Overall, mechanical bonding was the predominant bonding method, with metallurgical bonding as a supplementary bonding method within the coating and at the coating/substrate interface. There were no apparent pores and gaps between the particles in the mechanical bonding area and between the coating and the substrate. In regions of metallurgical bonding, adiabatic shear instability promoted the occurrence of dynamic recrystallization (DRX) on the one hand, leading to viscous flow of local materials, which damaged the original splat/substrate bonding surface and generating new bonding surfaces, on the other hand, promoted atomic diffusion between the coating and the substrate, allowing a close lattice match formed at the splat/substrate interface. Furthermore, the numerical simulation results of a single particle reflect, on the one hand, the plastic deformation occurred between the particles and the substrate during the deposition process, and on the other hand, the temperature at the metal jet increases in a short period of time, which made it possible for dynamic recrystallization to occur in this area. Therefore, the CS 2024Al coating exhibited excellent comprehensive properties with a porosity level of 0.31 ± 0.09%, a hardness of 157.3 ± 13.7 HV 0.025 , and an adhesion/cohesion strength exceeding 55.5 MPa. These properties were derived from the strong bonding among splats and between the splats and the substrate.
materials science, multidisciplinary,metallurgy & metallurgical engineering, characterization & testing