Abstract:This work reports a two-step constant-current anodization approach for the fabrication of an anodic aluminum oxide(AAO) template having an aspect ratio>1000.The effects of oxidation current densities and oxidation time on the morphologies,pore size,and thickness of AAO templates were studied.The results indicated that the morphology and thickness were significantly affected by both the oxidation time and the oxidation current density.High-quality AAO templates with 150-200 nm pore sizes,200 μm thicknesses,and 1000-1300 aspect ratios could be prepared under a constant-current density of 8 mA cm-2 and an oxidation time of 18 h.Using the AAO template,Ni nanowire arrays were fabricated by electrochemical deposition and were characterized by scanning electron microscopy(SEM),high resolution transmission electron microscopy(HRTEM),energy-dispersive X-ray spectroscopy(EDS),and X-ray diffraction(XRD) techniques.The Ni nanowire arrays were parallel to each other,with diameters of 150 nm,lengths of 180-200 μm,and aspect ratios of 1200-1300.These parameters compared favorably with those of the AAO template,thus indicating that it can be used for preparation of one-dimensional nanowire arrays with an ultrahigh aspect ratio.The effects of the aspect ratios on the magnetic characteristics of the Ni nanowire arrays were examined by comparing their coercivities and remanence ratios in parallel and perpendicular directions,respectively.The results indicated that Ni nanowire arrays with an aspect ratio>1000 clearly displayed a magnetic anisotropy,while the arrays with an aspect ratio of 200 did not.Thus an AAO template with an ultrahigh aspect ratio can be fabricated using a two-step constant-current anodization method,and that the AAO template may find applications in the fabrication of one-dimensional,high-aspect ratio nanowire arrays with special optical and magnetic properties.

Controlled Synthesis and Characteristics of Large-Area and High-Filling Nickel Nanowires Arrays in AAO Template

High-filling, large-area Ni nanowire arrays and the magnetic properties

Preparation of an Ultrahigh Aspect Ratio Anodic Aluminum Oxide Template for the Fabrication of Ni Nanowire Arrays

Controlled Synthesis and Magnetic Properties of Ni Nanotubes and Nanowires

Preparation and characterization of highly ordered NiO nanowire arrays by sol-gel template method

Controllable growth and magnetic characterization of electrodeposited nanocrystalline Ni–P alloy nanotube and nanowire arrays inside AAO template

Ordered Ni Nanowire Tip Arrays Sticking out of the Anodic Aluminum Oxide Template

Ni nanowires synthesized by microwave-assisted sol-gel template method

Large-scale Fabrication and Magnetic Properties of Ni8080Fe20 20 Nanowire Arrays

Study on Electrochemical Assembly of the Nanowire Array and Its Magnetic Properties

Electrodeposition and Magnetic Properties of Ni Nanowire Arrays on Anodic Aluminum Oxide/ti/si Substrate

Synthesis of Ordered Si Nanowire Arrays in Porous Anodic Aluminum Oxide Templates

Synthesis and Growth Mechanism of Ni Nanotubes and Nanowires

Single Crystal Ni5Zn21 Nanowire Arrays Fabricated by Electrodeposition in Anodic Alumina Membranes

Preparation of Pd-Ni alloy nanowires by AAO template

AAO-assisted Synthesis of Highly Ordered, Large-Scale TiO2 Nanowire Arrays Via Sputtering and Atomic Layer Deposition

Synthesis of high-ordered LiNi0.5Co0.5O2 nanowire arrays by AAO template and its structural properties

Orientation Growth and Magnetic Properties of Electrochemical Deposited Nickel Nanowire Arrays

Preparation and Magnetic Reseach of Co-Ni Alloy Nanowires Array

Large-area uniform nanodot arrays embedded in porous anodic alumina

Fabrication of large area nanodot arrays by assistance of low energy ion bombardment