Abstract:We demonstrate a simple and clean physical methodology for fabricating such nanoparticle assemblies (dense arrays and/or dendrites) related to the interfacial interaction between the constructed materials and the anodized aluminum oxide (AAO) porous templates. The interfacial interaction can be regulated by the surface tension of the constructed materials and the AAO membrane, and the AAO-template structure, such as pore size, membrane thickness and surface morphologies. Depending on the interfacial interaction between the constructed materials and the AAO templates, NP arrays with mean particle diameters from 3.8 ± 1.0 nm to 12.5 ± 2.9 nm, mean inter-edge spacings from 3.5 ± 1.4 nm to 7.9 ± 3.4 nm and areal densities from 5.6 × 10(11) NPs per cm(2) to 1.5 × 10(12) NPs per cm(2) are fabricated over large areas (currently ~2 cm × 3 cm). The fabrication process includes firstly thermal evaporation of metal layers no more than 10 nm thick on the pre-coated Si wafer by AAO templates with a thickness of less than 150 nm and mean pore sizes no more than 12 nm, and then removal of the AAO templates. The NP arrays can be stable for hours at a temperature slightly below the melting point of the constructed materials (e.g., ~800 °C for Au NPs for 4 hours) with little change in size and inter-particle separation. Using one of them (e.g., 11.8 nm Au NPs) as growth-oriented catalysts, ultra-thin (12.1 ± 2.3 nm) dense nanowires can be conveniently obtained. Furthermore, dendrite superstructures can be generated easily from eutectic alloy NPs with diameters of ~10 nm pre-formed by thermal evaporation of metal layers more than 20 nm thick on surface-patterned thick AAO templates (e.g., 500 nm). The resulting dendrites, dense arrays and other superstructures (i.e., nanorods and nanowires) formed using NP arrays as catalysts, should have broad applications in catalysis, information technology, photovoltaics and biomedical engineering.

Large-area uniform nanodot arrays embedded in porous anodic alumina

Fabrication of large area nanodot arrays by assistance of low energy ion bombardment

Optical Device Based on a Nanopillar Array by the Pattern Transfer of an Anodic Aluminum Oxide Membrane

Carbon Nanodot Arrays Grown As Replicas of Specially Widened Anodic Aluminum Oxide Pore Arrays

Fabrication and Application of Alumina Nanoscale Ordered Array Template

Large-area Fabrication of Periodic Fe Nanorings with Controllable Aspect Ratios in Porous Alumina Templates

Fabrication of a Regular Tripod Ni–P Nanorod Array and an AAO Template with Regular Branched Nanopores Using a Current-Controlled Branching Method

Growth of Highly-Ordered Metal Nanoparticle Arrays in the Dimpled Pores of an Anodic Aluminum Oxide Template

Controlled Synthesis and Characteristics of Large-Area and High-Filling Nickel Nanowires Arrays in AAO Template

Interface interaction induced ultra-dense nanoparticles assemblies

Fabrication of Si Nanodot Arrays by Plasma Enhanced CVD Using Porous Alumina Templates

Hydrophilicity reinforced adhesion of anodic alumina oxide template films to conducting substrates for facile fabrication of highly ordered nanorod arrays

Controllable Metal Nanodots Array Fabricatied by SDS-assisted Nanosphere Lithography and Its Application for Nanowires Growth

Magnetic Nanoparticle Arrays with Ultra-Uniform Length Electrodeposited in Highly Ordered Alumina Nanopores(“Alumite”)

AAO-assisted Synthesis of Highly Ordered, Large-Scale TiO2 Nanowire Arrays Via Sputtering and Atomic Layer Deposition

Field Emission Properties of Amorphous Carbon Nanodot Arrays in a Novel Anodic Aluminum Oxide Template by Self-Assembly Technique

Facile and Scalable Patterning of Sublithographic Scale Uniform Nanowires by Ultra-Thin AAO Free-Standing Membrane

Long-Range-Ordered Ag Nanodot Arrays Grown on Gaas Substrate Using Nanoporous Alumina Mask

High-filling, large-area Ni nanowire arrays and the magnetic properties

Photolithographic Approaches for Fabricating Highly Ordered Nanopatterned Arrays

Templated I‐pvd of Metallic Nanodot Arrays