Dislocation Arrangements Within Slip Bands During Fatigue Cracking

Linlin Li,Zhenjun Zhang,Peng Zhang,Cuihong Li,Zhefeng Zhang
DOI: https://doi.org/10.1016/j.matchar.2018.08.039
IF: 4.537
2018-01-01
Materials Characterization
Abstract:Microstructures and dislocations associated with the slip band (SB) fatigue cracks were investigated in Cu single crystal and bicrystal. It is found that there are high strain localizations with abundant dislocation cells around the cracked SBs. Due to the high local strain and slip irreversibility, the lattice rotates severely leading to large misorientation and hence low- or high- angle grain boundaries could form between the neighboring cells. Moreover, the dislocation walls can serve as preferential sites for nucleation and propagation of fatigue cracks with high density of dislocations, vacancies and high strain incompatibility.