Improved Depolarization Behavior and Electric Properties in (Bi0.5na0.5)tio3-Based Piezoelectric Composites

Xingru Zhang,Guicheng Jiang,Danqing Liu,Bin Yang,Wenwu Cao

DOI: https://doi.org/10.1016/j.jallcom.2018.08.043

IF: 6.2

2018-01-01

Journal of Alloys and Compounds

Abstract:(Bi0.5Na0.5)TiO3 (BNT) based ceramics have been restricted by the drawback of the low depolarization temperature T-d and ferroelectric-to-relaxor transition temperature TF-R. Many works have confirmed conventional improving strategies like doping and forming solid solution are not efficient to solve the problem. To overcome this obstacle, we introduced semiconductor ZnO into 0.93(Bi0.5Na0.5)TiO3-0.07Ba(Ti-0.945 Zr-0.055)O-3:xZnO matrix to prepare 0-3 type ceramic composites (abbreviated as BNTBZT:xZnO). Energy disperse spectroscopy (EDS) result reveals that there are two distributions of Zn. Most of Zn2+ ions gather around the boundaries of BNT-BZT grains to form ZnO enrichment regions, and the others diffuse into the lattice. In consideration of the fact that the distribution of Na also appears to be separated, a new model on the Na migration is proposed to explain experimental results. Both the substitution of lower valent Zn2+ ions at B site and the migration of Na are benefit for the formation of oxygen vacancies. As a consequence, the coercive field E-c and mechanical quality factor Q(m) have been significantly promoted. In terms of depolarization behavior, the temperature-dependent P-E loops show a completely different polarization process after ZnO incorporation. A slower decay of the remnant polarization P-r indicates ferroelectric state is more stable in the composites. The influence of internal bias field on asymmetric P-E loop has been discussed. The experiments on thermally stimulated depolarization current (TSDC) and temperature-dependent dielectric permittivity demonstrate T-d and TF-R increase about 17 degrees C and 19 degrees C, respectively. Our research confirms forming ZnO composites is an effective method to improve depolarization behavior, and BNT-BZT:xZnO composites should be an alternative for application in electromechanical devices. (C) 2018 Elsevier B.V. All rights reserved.