Effect of Discharge Energy on Micro-Arc Oxidation Coating of Zirconium Alloy
Wang,Lv,Du,Chen,Pang
DOI: https://doi.org/10.3390/ma17133166
IF: 3.4
2024-06-28
Materials
Abstract:The micro-arc oxidation (MAO) technique was used to grow in situ oxidation coating on the surface of R60705 zirconium alloy in Na2SiO3, Na2EDTA, and NaOH electrolytes. The thickness, surface morphology, cross-section morphology, wear resistance, composition, and structure of the micro-arc oxidation coating were analyzed by an eddy current thickness measuring instrument, XPS, XRD, scanning electron microscopy, energy spectrometer, and wear testing machine. The corrosion resistance of the coating was characterized by a polarization curve and electrochemical impedance spectroscopy (EIS). The results show that, with the increase in frequency, the single-pulse discharge energy decreases continuously, and the coating thickness shows a decreasing trend, from the highest value of 152 μm at 400 Hz to the lowest value of 87.5 μm at 1000 Hz. The discharge pore size on the surface of the coating gradually decreases, and the wear resistance and corrosion resistance of the coating first increase and then decrease. The corrosion resistance is the best when the frequency is 400 Hz. At this time, the corrosion potential is −0.215 V, and the corrosion current density is 2.546 × 10−8 A·cm−2. The micro-arc oxidation coating of zirconium alloy is mainly composed of monoclinic zirconia (m-ZrO2) and tetragonal zirconia (t-ZrO2), in which the content of monoclinic zirconia is significantly more than that of tetragonal zirconia.
materials science, multidisciplinary,metallurgy & metallurgical engineering,physics, applied,chemistry, physical, condensed matter