Effect of Discharge Energy on Micro-Arc Oxidation Coating of Zirconium Alloy

Wang,Lv,Du,Chen,Pang
DOI: https://doi.org/10.3390/ma17133166
IF: 3.4
2024-06-28
Materials
Abstract:The micro-arc oxidation (MAO) technique was used to grow in situ oxidation coating on the surface of R60705 zirconium alloy in Na2SiO3, Na2EDTA, and NaOH electrolytes. The thickness, surface morphology, cross-section morphology, wear resistance, composition, and structure of the micro-arc oxidation coating were analyzed by an eddy current thickness measuring instrument, XPS, XRD, scanning electron microscopy, energy spectrometer, and wear testing machine. The corrosion resistance of the coating was characterized by a polarization curve and electrochemical impedance spectroscopy (EIS). The results show that, with the increase in frequency, the single-pulse discharge energy decreases continuously, and the coating thickness shows a decreasing trend, from the highest value of 152 μm at 400 Hz to the lowest value of 87.5 μm at 1000 Hz. The discharge pore size on the surface of the coating gradually decreases, and the wear resistance and corrosion resistance of the coating first increase and then decrease. The corrosion resistance is the best when the frequency is 400 Hz. At this time, the corrosion potential is −0.215 V, and the corrosion current density is 2.546 × 10−8 A·cm−2. The micro-arc oxidation coating of zirconium alloy is mainly composed of monoclinic zirconia (m-ZrO2) and tetragonal zirconia (t-ZrO2), in which the content of monoclinic zirconia is significantly more than that of tetragonal zirconia.
materials science, multidisciplinary,metallurgy & metallurgical engineering,physics, applied,chemistry, physical, condensed matter
What problem does this paper attempt to address?
The problem that this paper attempts to solve is to explore the influence of single - pulse discharge energy on the performance of zirconium alloy micro - arc oxidation coatings. Specifically, the influence on coating thickness, surface morphology, wear resistance and corrosion resistance is studied by adjusting the pulse frequency. The paper aims to provide a comprehensive understanding of how single - pulse energy affects the overall performance of micro - arc oxidation coatings. ### Background of the Paper and Problem Description Zirconium alloys are widely used as special structural materials in the nuclear and chemical industries due to their low thermal neutron absorption cross - section, excellent high - temperature mechanical properties and good physicochemical compatibility. Therefore, high corrosion resistance is crucial for these applications. The service life of zirconium alloys in practical applications depends largely on their wear resistance and corrosion resistance. Surface modification techniques can significantly improve these properties, thereby prolonging the service life of zirconium alloys. Micro - arc oxidation (MAO) is a surface modification technique that can grow oxide coatings in - situ on the surfaces of aluminum, magnesium, titanium and zirconium and their alloys. MAO coatings are firmly bonded to the metal substrate and have excellent wear resistance, corrosion resistance and electrical insulation properties. Although MAO techniques for aluminum, magnesium, titanium and their alloys have been widely studied at home and abroad, relatively few studies on MAO of zirconium alloys have been carried out. ### Research Purpose This paper aims to study the influence of single - pulse discharge energy on the performance of zirconium alloy micro - arc oxidation coatings by adjusting the pulse frequency. By systematically analyzing the influence of frequency on coating thickness, surface morphology, wear resistance and corrosion resistance, a comprehensive understanding of how single - pulse energy affects the overall performance of MAO coatings is provided. ### Main Research Contents 1. **Experimental Methods**: - Use R60705 zirconium alloy as the substrate and prepare coatings at different frequencies by micro - arc oxidation technology. - Characterize the coatings by means of eddy - current thickness gauge, X - ray photoelectron spectroscopy (XPS), X - ray diffraction (XRD), scanning electron microscope (SEM), energy - dispersive spectrometer (EDS) and wear tester. - Test the corrosion resistance of the coatings by polarization curves and electrochemical impedance spectroscopy (EIS). 2. **Results and Discussions**: - **Coating Thickness**: As the frequency increases, the single - pulse discharge energy gradually decreases, and the coating thickness decreases from 152 μm at 400 Hz to 87.5 μm at 1000 Hz. - **Surface Morphology**: As the frequency increases, the pore diameter on the coating surface gradually decreases and the surface roughness decreases, but when the frequency is too high, gullies will appear on the coating surface. - **Wear Resistance**: The wear resistance of the coating first increases and then decreases, and the best wear resistance occurs at 400 Hz. - **Corrosion Resistance**: The corrosion resistance of the coating also first increases and then decreases, and the best corrosion resistance also occurs at 400 Hz. At this time, the corrosion potential is −0.215 V and the corrosion current density is 2.546 × 10^−8 A·cm^−2. ### Conclusions By adjusting the pulse frequency, the single - pulse discharge energy can be effectively controlled, thereby optimizing the performance of zirconium alloy micro - arc oxidation coatings. At 400 Hz, the coating thickness, surface morphology, wear resistance and corrosion resistance all reach the best state. This research provides an important reference basis for the surface modification of zirconium alloys.