Abstract:PANI/FeS2/MnO2 composite electrode materials were successfully prepared. The results showed that the specific capacitance of PANI/FeS2/MnO2 4 : 1 : 3 was 580 F/g at 1 A/g, and the capacitance retention rate was 85.2 % after cycling 10,000 times at 5 A/g. The asymmetric supercapacitor PANI/FeS2/MnO2 4 : 1 : 3 //AC had an energy density of 37.93 Wh/kg at a power density of 0.85 kW/kg. Polyaniline (PANI) has unique physical and chemical peculiarities, so it has been widely researched in the field of energy storage. However, its structure is easy to be damaged during charging and discharging, which seriously affects its application. PANI/FeS2/MnO2 composite materials were successfully prepared by an easy combination of chemical precipitation and chemical oxidative polymerization. The electrochemical test results manifested that the specific capacitance of PANI/FeS2/MnO2 4 : 1 : 3 was 580 F/g at 1 A/g, and had great cyclic stability (capacitance retention rate was 85.2 % after 10000 cycles at 5 A/g). It was because that reticular structure shortened the ion transport path. On the other hand, it was able to effectively mitigate the volume change during long‐term charging and discharging, thus improving the cycling stability. In addition, PANI/FeS2/MnO2 4 : 1 : 3 as the positive and activated carbon (AC) as the negative, an asymmetrical supercapacitor was assembled with a maximal energy density of 37.93 Wh/kg when its power density was 0.85 kW/kg. At the same time, the device possessed a long cycle life (the capacitance conservation rate was 82 % after 5000 cycles at 5 A/g). This excellent performance is due to the excellent synergy between the PANI, FeS2 and MnO2. This study opens a new way to investigate polyaniline‐based composite electrode materials.

Deposition of Polyaniline on Porous ZnFe2O4 As Electrode for Enhanced Performance Supercapacitor

Development of PANI/FeS2/MnO2 Composite Electrode Materials for High‐Performance Supercapacitors

Polyaniline-deposited porous carbon electrode for supercapacitor

Preparation of Polyaniline/activated Carbon Used for Supercapacitor Film Electrode by Cyclic Voltammetry

In-situ Electropolymerization of Porous Conducting Polyaniline Fibrous Network for Solid-State Supercapacitor

Electrochemical Deposition of PANI/PEDOT:PSS Composite Polymer for Supercapacitors Application

Construction of tunable ZnCoO x /C-PANI electrode materials for high-performance supercapacitors

Facile Synthesis of a Ni-based NiCo2O4-PANI Composite for Ultrahigh Specific Capacitance

Activated Carbon Coated with Polyaniline As an Electrode Material in Supercapacitors

Synthesis of Biomass-Based Porous Carbon Nanofibre/Polyaniline Composites for Supercapacitor Electrode Materials

Graphene/Polyaniline Nanofiber Composites as Supercapacitor Electrodes

Polyaniline – Cobalt Hexacyanoferrate Composites as High‐Performance Cathodes for Zn‐ion Hybrid Supercapacitor

Vapor deposition polymerization of aniline on 3D hierarchical porous carbon with enhanced cycling stability as supercapacitor electrode

A new nanocomposite: Carbon cloth based polyaniline for an electrochemical supercapacitor

Electrochemical evaluation of ZnO and PAN-based carbon nanofibers composite for high-performance supercapacitor application

Polyaniline/SnO2 nanocomposite for supercapacitor applications

Synthesis of Polyaniline Nanoparticles Deposited on Two-Dimensional Titanium Carbide for High-Performance Supercapacitors

Facile Fabrication of Polyaniline/Pbs Nanocomposite for High-Performance Supercapacitor Application

Electrodeposition of PANI/MnO2 Composite on SnO2/Ti Substrate for Supercapacitor Electrode

Hierarchically Porous Carbon Cloth–Polyaniline (CC–PANI) Composite Supercapacitor Electrodes with Enhanced Stability

(Metal-Organic Framework)-Polyaniline sandwich structure composites as novel hybrid electrode materials for high-performance supercapacitor