A high-performance TiO 2 nanotube supercapacitor by tuning heating rate during H 2 thermal annealing

Cheng Zhang,Liyi Li,Chia-Chi Tuan,Jian Zhou,Feng Xue,Ching-Ping Wong

DOI: https://doi.org/10.1007/s10854-018-9654-3

2018-01-01

Abstract:TiO 2 nanotube is a promising material for supercapacitor electrodes. Thermal annealing has been proved as an effective way enhancing the performance of TiO 2 nanotube supercapacitors. However, heating rate, as an important parameter in the thermal annealing, has been overlooked as a factor that can influence the electrochemical performance of TiO 2 nanotube supercapacitors. In this paper, we demonstrate that the electrochemical performance of TiO 2 nanotube supercapacitors fabricated by anodization process can be significantly improved by tuning heating rate during hydrogen thermal annealing. At the optimal condition, the areal capacitance of TiO 2 nanotube supercapacitors increased from 27.36 to 52.40 mF cm −2 with a scan rate of 100 mV s −1 , while maintaining a high capacitance retention of 65.9% when the scan rate increased from 10 to 1000 mV s −1 . Moreover, outstanding long-term cycling stability with only 4.8% capacitance reduction after 5000 charge–discharge cycles is observed. It is found that the electronic carrier densities, surface hydroxyl group density, as well as crystallite size in TiO 2 are maximized at the optimal annealing condition, all of which are accounted for the enhancement of the electrochemical performance.