Effect of Heat Treatment Temperature on Microstructure, Tensile Properties and δ-Precipitate Phase in Ni-based Superalloy
Jeonyoung Song,Jiho Gu,Jiho Gu,Won Hui Jo,Cho Hyeon Lee,Jae Bok Seol,Youngwha Ma
DOI: https://doi.org/10.3365/kjmm.2024.62.1.32
IF: 1.324
2024-01-05
Korean Journal of Metals and Materials
Abstract:Here, we investigated the influence of δ-precipitate (orthorhombic D0a Ni 3 Nb-ordered phase) on the room- and high-temperature tensile properties in wrought nickel-based Inconel 625 superalloys subjected to solution and aging heat treatment. Typically, solution heat-treatment temperatures in these alloys affect the solid-state precipitation of δ-phase, which governs high-temperature tensile properties. While precipitation of fine D0 a δ-phase is known to have beneficial effects on the mechanical properties owing to the retardation of grain coarsening, Widmanstätten δ precipitation plays a deleterious influence on the fracture toughness, tensile ductility, and fatigue resistance. Therefore, to enhance the mechanical properties of this alloy series, it is key to generate a high number density of fine D0 a δ precipitate by adjusting solid solution treatment temperatures. In this study, solution heat treatments were conducted above and below δ-phase solvus temperatures. By applying solution heat treatment at 900°C and 970°C, this alloy was confirmed to have a Widmanstätten δ phase and is composed similarly to the annealed microstructure. This Widmanstätten δ precipitate was densely distributed at both intergranular and intragranular grains. On the other hand, when solution treatment was applied at 1040 and 1100°C, more coarse particles (approximately 30 μm) with a significant reduction of Widmanstätten type δ phase were obtained. We found that grain size and Widmanstätten δ-phases have an important role in the high-temperature tensile properties of Inconel 625 superalloy series.
materials science, multidisciplinary,metallurgy & metallurgical engineering