Effect of Solution Temperature on Microstructure and Mechanical Properties of Ti–5Al5Mo5V3Cr1Zr Alloy
Feiyu Huang,Chaowen Huang,Mingpan Wan,Shewei Xin,Yongqing Zhao,Tao Wang,Shengli Ji,Weidong Zeng
DOI: https://doi.org/10.1002/adem.202200003
IF: 3.6
2022-04-24
Advanced Engineering Materials
Abstract:The purpose of this work is to reveal the relationship between the solution temperature, microstructure, and mechanical properties of the Ti‐5Al5Mo5V3Cr1Zr (Ti‐55531) alloy. The alloys were prepared via solution processing in a temperature ranging from Tβ–100 °C (where Tβ is the β‐transus temperature) to Tβ+ 100 °C for 2 h; they were then air cooled, aged at 600 °C for 6 h and air cooled again. The results indicate that the whole solution temperature range (Tβ–100 °C to Tβ+100 °C) can be divided into the following five ranges according to the performance of the Ti‐55531 alloy. The alloy presents an excellent mechanical performance combining a high strength and a good ductility for solution temperatures ranging from Tβ–50 °C to Tβ–30 °C and from Tβ +10 °C to Tβ+30 °C. Interestingly, the Ti‐55531 alloy exhibits a dramatically enhanced strength, while the ductility drops rapidly as the solution temperature exceeds Tβ+70 °C. The enhanced strength main reason is the grain boundary α phase changes from continuous to discontinuous with increasing solution temperature in this temperature range, nevertheless, the increased size of β grains result a reduction in the ductility. Thus, the continuity of grain boundary α phase has a dramatical influence on performance of Ti‐55531 alloy.This article is protected by copyright. All rights reserved.
materials science, multidisciplinary