Abstract:Static and dynamic mechanical properties of cement-asphalt composites with various contents of asphalt incorporated were studied. Uniaxial compressive stress-strain curves of different cement-asphalt mortars (CAMs) with cement mass ratio (A/C) in the range of 0.2 to 1.0 were obtained by the Materials Testing System (MTS) under different testing temperatures ranging from -40 to 80 degrees C. Two typical CAMs, one with A/C of 0.2 denoted by LAC and the other with A/C of 0.9 denoted by HAC, were chosen to be tested at varied deformation rates over a range of 0.3 to 30 mm/min at room temperature. The correlation between mechanical properties, e.g., peak stress or elastic modulus, and temperature or loading rate was, respectively, acquired. As a result, temperature sensitivity and loading rate dependence for mechanical behavior of different CAMs were analyzed. Dynamic mechanical analysis (DMA) on three cement-asphalt binders (CABs) with A/Cs from 0.2 to 1.0 was carried out, and temperature spectra and frequency spectra were obtained. The Burger model was used to simulate the viscoelastic mechanical behaviors of CABs. Results indicate that peak stress and elastic modulus of CAMs decline with the increasing A/C and temperature. The temperature sensitivity and the loading rate dependence for mechanical properties of CAMs with higher A/Cs are greater than those of CAMs with lower A/Cs. To quantify the dependence of mechanical properties on temperature and loading rate, temperature-sensitive factor and rate-influencing factor are defined separately. The two factors increase with the A/C, implying that CAMs with higher A/Cs have greater dependence on temperature and loading rate. Furthermore, the two factors for peak stress are bigger than those for elastic modulus for a given CAM. Dynamic modulus of CABs descends with the increase of A/C or temperature but ascends with the loading frequency. As the temperature rises or A/C increases, the viscoelasticity becomes more remarkable. The dependence of dynamic modulus of CABs with varied A/Cs on loading frequency is successfully simulated by using the Burger model.

Modeling Mechanical Properties of Cement Asphalt Emulsion Mortar with Different Asphalt to Cement Ratios and Temperatures

Static and Dynamic Mechanical Properties of Cement-Asphalt Composites

Influences of Temperature on Mechanical Properties of Cement Asphalt Mortars

Static and dynamic mechanical behavior of cement asphalt mortars

TEMPERATURE SENSITIVITY OF MECHANICAL PROPERTIES OF CEMENT ASPHALT MORTARS

A New Dynamic Modulus Predictive Model for Asphalt Mixtures Based on the Law of Mixtures

Prediction of Dynamic Shear Modulus of Fine Aggregate Matrix Using Discrete Element Method and Modified Hirsch Model

A Study on Mechanical Performance and Mechanism of Cement Asphalt Mortar

Comparative Modelling of Indirect Tensile Strength of Asphalt Mixtures with and Without Considering Air Void Characteristics

Research on Factors Influencing Mechanical Properties of High Strength Cement Asphalt Mortar and Mechanical Mechanism

Cement Asphalt Mastic Dynamic Mechanical Properties and Microstructure Research

Influence of Loading Rate on Mechanical Properties of Cement Asphalt Mortars

Effect of Curing Temperature on Strength Development of Cement-Asphalt Mortars

Influence of cationic asphalt emulsion on the water transportation behavior and durability of cement mortar

Strength Mechanism of Cement-Asphalt Mortar

Compressive Strength Development and Microstructure of Cement-Asphalt Mortar

The Mechanical Properties of Polymer-cement Mortar

Cement Hydration Based Model to Predict the Mechanical Properties of Precast Concrete

Research on Factors Influencing Compressive Strength of High Strength Cement Asphalt(CA)Mortar

Modified Two-Phase Micromechanical Model and Generalized Self-Consistent Model for Predicting Dynamic Modulus of Asphalt Concrete

Fracture Parameters and Influencing Factors of Cement Asphalt Mortar