Crystal Growth, Spectroscopy and First Laser Operation of a Novel Disordered Tetragonal Tm:Na2La4(WO4)7 Tungstate Crystal

Lizhen Zhang,Shijia Sun,Zhoubin Lin,Haifeng Lin,Ge Zhang,Xavier Mateos,Josep Maria Serres,Magdalena Aguilo,Francesc Diaz,Pavel Loiko,Yicheng Wang,Uwe Griebner,Valentin Petrov,Elena Vilejshikova,Weidong Chen
DOI: https://doi.org/10.1016/j.jlumin.2018.07.016
IF: 3.6
2018-01-01
Journal of Luminescence
Abstract:Tm3+:Na2La4(WO4)(7), a disordered tetragonal scheelite-type tungstate crystal, is grown by the Czochralski method. The polarized absorption, stimulated-emission and gain cross-section spectra are determined. The maximum sigma(SE) is 1.62 x 10(-20) cm(2) at 1788.6 nm for sigma-polarization. The Judd-Ofelt parameters for Tm3+ are Omega(2) = 10.321, Omega(4) = 0.183 and Omega(6) = 2.122 [10(-20) cm(2)]. The radiative lifetime of the F-3(4) state is 1.63 ms. Raman spectroscopy reveals a maximum phonon energy of 923 cm(-1). Laser operation under diode-pumping is achieved with both a-cut and c-cut Tm:Na2La4(WO4)(7) crystals, reaching a maximum output power for the a-cut of 715 mW at similar to 1937 nm with a slope efficiency of 34%. Microchip laser operation using the c-cut crystal yields a slope efficiency of 41%. The Tm:Na2La4(WO4)(7) crystal is promising for mode-locked lasers due to its broadband emission.
What problem does this paper attempt to address?