Abstract:Intumescent flame retardants (IFR) with phosphorus (P)/nitrogen (N)-containing diphenols (DH, DV and DS) were synthesized from p-hydroxybenzaldehyde (H), vanillin (V) and syringaldehyde (S) with different methoxyl groups on its aromatic ring. The FTIR, 1H NMR, 13C NMR, XPS methods were used to characterize the structures of IFR, and LOI, CCT, SEM, TG methods were used to investigate the flame retardancy and thermal stability of rigid polyurethane (RPU) foams when the three IFR were incorporated into RPU foams. Compared with H, V and S, the DH, DV and DS FTIR spectra showed absorption peaks at 3450 cm−1, 1160 cm−1, and 1222 cm−1, 1050 cm−1 and 740 cm−1, respectively, which attributed to NH, CN, and P = O, P-O, P-C groups. The 1H NMR spectra of DH, DV and DS showed proton signals at 4.8 and 6.0 ppm, which were corresponding to H1 and H2 of CN groups, and corresponding C1 signal appeared around 62.3 ppm in the 13C NMR spectra. The XPS spectra of DH, DV, DS showed peaks at 285, 398 eV and 133.5, 532 eV, which may be due to corresponding C1s, N1s of CN groups and P2p and O1s of P-O-C groups, respectively. These results indicated that the target compounds P/N-containing diphenols DH, DV and DS were synthesized successfully. Flame retardancy index (FRI) values of RPU-DH, RPU-DV, and RPU-DS were 2.33, 2.30 and 2.43, respectively, suggesting that DH, DV, and DS were good flame retardant additives. The THR and HRR values of RPU-DH, RPU-DV, RPU-DS foams were much lower than that of RPU foam. The fire growth rate (FIGRA) of RPU-DH, RPU-DV, and RPU-DS was 29.4%, 30.3%, and 24.4% lower comparing to RPU foam. The LOI value of RPU foam was 19%, while LOI values of RPU-DH, RPU-DV and RPU-DS foams increased to around 26%. These results suggested that the flame retardancy of RPU foams were improved by incorporating DH, DV, and DS. Compared with RPU foam, the CY600 of RPU-DH, RPU-DV and RPU-DS foams increased by 215.2%, 152.2% and 195.6%, respectively, and the char residue after CCT were much compact and homogeneous, which could reduce heat and mass transfer, protecting underlying materials from further combustion in a fire. In conclusion, the P/N-containing diphenols DH, DV and DS were synthesized successfully, and they were good flame retardant additives. The char residue of RPU-DH, RPU-DV and RPU-DS foams increased remarkably, and formed compact and homogeneous char layer. The flame retardancy and thermal stability of RPU-DH, RPU-DV, RPU-DS foams were improved by incorporating DH, DV, and DS.

Full Substitution of Petroleum-Based Polyols by Phosphorus-Containing Soy-Based Polyols for Fabricating Highly Flame-Retardant Polyisocyanurate Foams

Preparation and properties of bio‐based flame‐retardant rigid polyurethane foams with soybean oil polyols containing phosphorus

Synthesis of reactive DOPO-based flame retardant and its application in rigid polyisocyanurate-polyurethane foam

Phosphorus-containing soybean oil-derived polyols for flame-retardant and smoke-suppressant rigid polyurethane foams

Fabrication of Fire Safe Rigid Polyurethane Foam with Reduced Release of CO and NOx and Excellent Physical Properties by Combining Phosphine Oxide-Containing Hyperbranched Polyol and Expandable Graphite

Preparation of flame‐retardant rigid polyurethane foam with bio‐based phosphorus‐containing polyols and expandable graphite

Biobased Phosphorus Siloxane-Containing Polyurethane Foam with Flame-Retardant and Smoke-Suppressant Performances

Flame retardant flexible polyurethane foams based on phosphorous soybean-oil polyol and expandable graphite

Fabrication of Rigid Isocyanate-Based Polyimide Foam Achieved Excellent Use Safety via Synergy between Expandable Graphite and Phosphorus-Containing Polyol

Highly-efficient Reinforcement and Flame Retardancy of Rigid Polyurethane Foam with Phosphorus-Containing Additive and Nitrogen-Containing Compound

A novel phosphorus-modified silica aerogel for simultaneously improvement of flame retardancy, mechanical and thermal insulation properties in rigid polyurethane foam

Preparation and intrinsical flame resistance of reed-based polyurethane foam modified by 9,10-dihydro-9-oxa-10 phosphaphenanthrene 10-oxide

Synthesis of Phosphorus–Sulfur-Containing Polyols for Intrinsic Flame Retardant Flexible Polyurethane Foams with Enhanced Mechanical Properties

Rosin‐Based Si/P‐Containing Flame Retardant Toward Enhanced Fire Safety Polyurethane Foam

Diphase Flame‐retardant Effect of Ammonium Polyphosphate and Dimethyl Methyl Phosphonate on Polyisocyanurate‐polyurethane Foam

Synthesis of phosphorus/nitrogen containing intumescent flame retardants from p-hydroxybenzaldehyde, vanillin and syringaldehyde for rigid polyurethane foams

Phosphorus and Nitrogen-Containing Polyols: Synergistic Effect on the Thermal Property and Flame Retardancy of Rigid Polyurethane Foam Composites

Fabrication of nickel phytate modified bio-based polyol rigid polyurethane foam with enhanced compression-resistant and improved flame-retardant

A novel halogen-free flame-retardant fabrication for the study of smoke suppression and flame retardancy of polystyrene

Enhanced Fire Safety of Rigid Polyurethane Foam via Synergistic Effect of Phosphorus/Nitrogen Compounds and Expandable Graphite

Engineering Sulfur-Containing Polymeric Fire-Retardant Coatings for Fire-Safe Rigid Polyurethane Foam