Bioinspired, Highly Adhesive, Nanostructured Polymeric Coatings for Superhydrophobic Fire-Extinguishing Thermal Insulation Foam
Zhewen Ma,Xiaochen Liu,Xiaodong Xu,Lei Liu,Bin Yu,Cristian Maluk,Guobo Huang,Hao Wang,Pingan Song
DOI: https://doi.org/10.1021/acsnano.1c02254
IF: 17.1
2021-06-25
ACS Nano
Abstract:Lightweight polymeric foam is highly attractive as thermal insulation materials for energy-saving buildings but is plagued by its inherent flammability. Fire-retardant coatings are suggested as an effective means to solve this problem. However, most of the existing fire-retardant coatings suffer from poor interfacial adhesion to polymeric foam during use. In nature, snails and tree frogs exhibit strong adhesion to a variety of surfaces by interfacial hydrogen-bonding and mechanical interlocking, respectively. Inspired by their adhesion mechanisms, we herein rationally design fire-retardant polymeric coatings with phase-separated micro/nanostructures <i>via</i> a facile radical copolymerization of hydroxyethyl acrylate (HEA) and sodium vinylsulfonate (VS). The resultant waterborne poly(VS-<i>co</i>-HEA) copolymers exhibit strong interfacial adhesion to rigid polyurethane (PU) foam and other substrates, better than most of the current adhesives because of the combination of interfacial hydrogen-bonding and mechanical interlocking. Besides a superhydrophobic feature, the poly(VS-<i>co</i>-HEA)-coated PU foam can self-extinguish a flame, exhibiting a desired V-0 rating during vertical burning and low heat and smoke release due to its high charring capability, which is superior to its previous counterparts. Moreover, the foam thermal insulation is well-preserved and agrees well with theoretical calculations. This work offers a facile biomimetic strategy for creating advanced adhesive fire-retardant polymeric coatings for many flammable substrates.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsnano.1c02254?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsnano.1c02254</a>.Supplementary experimental procedure: determination of reactivity ratios, and characterizations. Figures S1–S38: digital photos of aqueous solutions, IR, <sup>1</sup>H NMR spectra, viscoelastic, digital photos, SEM and TEM images, friction, optical photos, UV aging, tensile results, DSC, TGA, HRR, shear strength of coatings; adhesive and adhesion mechanism; hydrophobic features and contact angles; compression properties of coatings and foams; digital photos for samples after burning, HRR, CO<sub>2</sub> and CO production, smoke density of foams; HRR curves and char morphology of wood, epoxy resin, and PLA; Py-GC/MS results, thermal conductivity of foam samples; LOI values and SEM images of HGM-modified fire-retardant RPF. Tables S1–S8: elemental analysis, molecular weight, thermal and flammability properties of fire-retardant coatings; detailed fire-retardant parameters for PU foam and other materials; the use amount of coating for samples; elemental compositions of chars; detailed thermal conductivity data for coatings and foams (<a class="ext-link" href="/doi/suppl/10.1021/acsnano.1c02254/suppl_file/nn1c02254_si_001.pdf">PDF</a>)Movie S1: flammability testing by using an alcohol lamp (<a class="ext-link" href="/doi/suppl/10.1021/acsnano.1c02254/suppl_file/nn1c02254_si_002.mp4">MP4</a>)Movie S2: flammability testing by using a UL-94 tester (<a class="ext-link" href="/doi/suppl/10.1021/acsnano.1c02254/suppl_file/nn1c02254_si_003.mp4">MP4</a>)This article has not yet been cited by other publications.
materials science, multidisciplinary,chemistry, physical,nanoscience & nanotechnology