Study on the Friction Reducing Effect of Graphene Coating Prepared by Electrophoretic Deposition

Hong,Sulin Chen,Xi Chen,Zhinan Zhang,Bin Shen

DOI: https://doi.org/10.1016/j.procir.2018.05.037

2018-01-01

Procedia CIRP

Abstract:The present study presents the promising friction reducing effect of electrophoretic deposition (EPD) prepared graphene coating when it is utilized as a solid lubricant on the surface of silicon wafer. Graphene coatings with various surface morphology and microstructures are fabricated by adopting different combinations of applied voltage and deposition duration in EPD process and characterized by SEM, Raman and XPS. Their frictional behaviors are investigated in a set of ball-on-plate reciprocating friction tests conducted in ambient air condition (50-80%RH), in which silicon nitride balls (Φ4 mm) are used as the counterpart material. Moreover, the influence of the normal load on the friction reducing effect of graphene coating is examined. The results show that the coefficients of friction (COF) of graphene coated silicon wafer presents a steady-state value around 0.08-0.1, reduced by over 80% compared with that of the bare silicon, around 0.6. It is noted that changing EPD parameters or normal loads only affects the durability of friction reducing effect of the fabricated graphene coating, but does not show discernable influence on the extent of the reduction in the steady-state COF. The examination on the worn surface within the wear tracks on both the graphene coated silicon and its counterface suggest that the formation of graphene-containing transfer layer on the sliding interface is a critical and necessary condition for the presence of such stable low-friction sliding period. Once they are removed from the sliding interface or worn out, the friction reducing effect disappears. Compared with increasing the EPD voltage, elongating the deposition duration at low voltage in the EPD process, which could produce graphene coatings with more compact microstructure, is proved to be a more effective approach to enhance the durability and load capacity of the graphene coating as a solid lubricant.