Abstract:Two polyelectrolytes, i.e., cationic poly(diallydimethylammonium chloride) (PDDA) and anionic sodium poly(4-styrenesulfonate) (PSSNa), were separately mixed with graphene oxide (GO) and hydrazine in solution, and heat-treated to result in composites of PDDA/graphene (GN) and PSSNa/GN, respectively. The composites were characterized by scanning electron microscopy, transmittance electron microscopy and Raman spectroscopy. Impedance-type humidity sensors were constructed by depositing the composite films onto interdigitated gold electrodes via dip-coating. The electrical response of the composite humidity sensors toward relative humidity (RH) was investigated at room temperature. It was found that the composites with higher content of GN exhibited lower impedance at low humidity levels. Both composite sensors could detect very low humidity (down to 0.2%RH), and showed good response magnitude in the low humidity range (relative impedance change of 300% and 1000% from 0.2 to 30%RH for PSSNa/GN and PDDA/GN, respectively). Moreover, the composites exhibited slight hysteresis similar to that of the polyelectrolytes alone, while their response time for desorption was even reduced. The sensing mechanism of the composites was explored by complex impedance spectra analysis, and the good sensing behavior at low humidity was proposed to the special electrical property and unique two-dimensional nanosheet structure of GN.

Humidity Sensing Properties of the Composite of Electrospun Crosslinked Polyelectrolyte Nanofibers Decorated with Ag Nanoparticles

Electrospun nanofibers of polymer composite as a promising humidity sensitive material

Bilayer-structured Nanocomposite of Ag and Crosslinked Polyelectrolyte for the Detection of Humidity

A composite of quaternized and crosslinked poly(4-vinylpyridine) with processable polypyrrole for the construction of humidity sensors with improved sensing properties

Crosslinked and quaternized poly(4-vinylpyridine)/polypyrrole composite as a potential candidate for the detection of low humidity.

Preparation of Nanocomposite of Graphene and Quaternized Poly(4-vinylpyridine)and investigations on its humidity sensory properties

A Novel Humidity Sensor Based on Carbon Black/poly(4-vinylpyridine) Nanocomposite

A RESISTIVE-TYPE NANOSTRUCTURED HUMIDITY SENSOR PREPARED BY ELECTROSPINNING

Poly(4-vinylpyridine)/carbon Black Composite As a Humidity Sensor

Highly Sensitive and Ultrafast Response Surface Acoustic Wave Humidity Sensor Based on Electrospun Polyaniline/poly(vinyl Butyral) Nanofibers.

A humidity sensor based on interpenetrating polymer network prepared from poly(dimethylaminoethyl methacrylate) and poly(glycidyl methacrylate)

Investigations on the sensing mechanism of humidity sensors based on electrospun polymer nanofibers

Polyaniline Nanofiber Humidity Sensor Prepared by Electrospinning

Facilely prepared composites of polyelectrolytes and graphene as the sensing materials for the detection of very low humidity

Humidity sensors based on the composite of multi-walled carbon nanotubes and crosslinked polyelectrolyte with good sensitivity and capability of detecting low humidity

Humidity Sensors Using in Situ Synthesized Sodium Polystyrenesulfonate/zno Nanocomposites.

The Electrical Responses to Humidity of a Composite of Polyaniline and Polyelectrolyte

Humidity sensitive properties of crosslinked and quaternized poly(4-vinylpyridine-co-butyl methacrylate)

A highly sensitive humidity sensor based on a nanofibrous membrane coated quartz crystal microbalance

Bilayer Composite Humidity Sensor Based on Polyaniline and Polyelectrolyte

Highly Sensitive Humidity Sensors Based on Polyethylene Oxide/CuO/Multi Walled Carbon Nanotubes Composite Nanofibers