Abstract:Developing ultra-high strength in rare-earth-free Mg alloys using conventional extrusion process is a great challenge. What is even more difficult is to achieve such a goal at a lower processing cost. In this work, we report a novel low-alloyed Mg-2Sn-2Ca alloy (in wt. %) that exhibits tunable ultra-high tensile yield strength (360–440 MPa) depending on extrusion parameters. More importantly, there is little drop in mechanical properties of this alloy even when it is extruded at a speed several times higher than those used in the reported high strength Mg alloys. Examination of as-extruded microstructures of this Ca-containing Mg alloy reveals that the ultra-high strength is mainly associated with the presence of surprisingly submicron matrix grains (down to ∼0.32 μm). The results suggest that the Ca addition promotes accumulations of the pyramidal dislocations, which eventually transform into the low angular grain boundaries (LAGBs). The high number density of LAGBs separate the α-Mg matrix via either discontinuous dynamic recrystallization (DDRX) mechanism in the early stage or the continuous dynamic recrystallization (CDRX) mechanism in the later stage of extrusion, which effectively enhances the nucleation rates of the DRXed grains. More importantly, large amount of Ca segregation along LAGBs, accompanied with dynamically precipitated Mg2Ca nano-phases, are detected in the present non-severely deformed samples. It is the combination of solute segregations and numerous Mg2Ca nano-precipitates that contributes to the formation of the ultra-fine grains via pinning mechanism. The ultrafine grains size, Ca enrichment in most LAGBs, and residual Mg2Ca nano-precipitates would in turn contribute significantly to the enhancement of the yield strength of the as-extruded Mg-2Sn-2Ca (wt.%) alloy. The low content of alloying elements and the fast one-step extrusion process render the present alloys low-cost and thus have great potential in large-scale industry applications.

Fabrication of Ultra-High Strength Magnesium Alloys over 540 MPa with Low Alloying Concentration by Double Continuously Extrusion

Microstructure, Mechanical Properties, Biocorrosion Behavior, and Cytotoxicity of As-Extruded Mg–Nd–Zn–Zr Alloy with Different Extrusion Ratios

Microstructure and Mechanical Properties of Double Continuously Extruded Mg–Zn–Gd-based Magnesium Alloys

Fabrication of magnesium alloy with high strength and heat-resistance by hot extrusion and ageing

Achieving superior mechanical properties in a low-alloyed magnesium alloy via low-temperature extrusion

Ultrahigh Strength Mg-Al-Ca-Mn Extrusion Alloys with Various Aluminum Contents

Origins of High Ductility Exhibited by an Extruded Magnesium Alloy Mg-1.8Zn-0.2Ca: Experiments and Crystal Plasticity Modeling

Fabrication of high strength-ductility Mg-3.8Al-1.1Sn-0.4Ca alloy via differential-thermal asymmetric extrusion

Effects of Extrusion and Heat Treatment on the Mechanical Properties and Biocorrosion Behaviors of A Mg-Nd-Zn-Zr Alloy

The Development of a High-Strength Mg-10.3Gd-4.4Y-0.9Zn-0.7Mn Alloy Subjected to Large Differential-Thermal Extrusion and Isothermal Aging

Fabrication of high-strength Mg-Gd-Zn-Zr alloys via differential-thermal extrusion

Microstructure and Mechanical Properties of Mg–4.0Zn–0.5Ca Alloy

Development of low-alloyed and rare-earth-free magnesium alloys having ultra-high strength

Enhanced Mechanical Properties in Fine-Grained Mg–1.0Zn–0.5Ca Alloys Prepared by Extrusion at Different Temperatures

Mechanical Properties and Biocorrosion Resistance of Mg-Nd-Zn-Zr Alloy Improved by Cyclic Extrusion and Compression

Realizing ultra-fine grains and ultra-high strength in conventionally extruded Mg-Ca-Al-Zn-Mn alloys: The multiple roles of nano-precipitations

Improvement of Mechanical Properties and Corrosion Resistance of Biodegradable Mg–Nd–Zn–Zr Alloys by Double Extrusion

Optimization of Microstructure and Mechanical Property of a Mg-Zn-Y-Nd Alloy by Extrusion Process

Achieving exceptional ultrahigh-strength in low-alloy Mg-1Al-1Ca-0.4Mn (wt%) alloy by regulating bimodal microstructure

High-performance Mg-Zn alloy achieved by the ultrafine grain and nanoparticle design

Superior Strength-Ductility Synergy of Mg-Nd-Zn-Zr Alloy Rod Achieved by Drawing at Elevated Temperatures