High color‐purity broad orange‐red emission of Mn2+‐doped transparent phosphate glass–ceramics embedded NaYP2O7 crystals
Haozhang Liang,Xiangtao Lin,Nanshan Ma,Longqing He,Juxia Tong,Zhiwei Luo,Lingying Ye,Anxian Lu
DOI: https://doi.org/10.1111/jace.19786
IF: 4.186
2024-03-20
Journal of the American Ceramic Society
Abstract:The Mn2+‐doped transparent NaYP2O7 glass–ceramics generates a broad emission at 620 nm (4T2(g)→6A1(s)) with a full width at half‐maximum of ∼107 nm under the excitation of 408 nm. The time‐resolved emission spectra and temperature‐dependent emission spectra show that Mn2+‐doped NaYP2O7 glass–ceramic exhibits stable orange‐red luminescence with the chromaticity coordinates of (0.5684, 0.4275), low correlated color temperature of 1 800 K, high color‐purity of 98.88%, and low thermal quenching (70% at 373 K), which can be used for high color‐purity orange‐red display devices. In this work, novel Mn2+‐doped transparent NaYP2O7 glass–ceramics were prepared through melt‐quenching and subsequent thermal treatment. The surface crystallization method was confirmed based on the differential scanning calorimeter, X‐ray diffraction, and scanning electron microscope characterization. As the increase and prolong of the heat‐treatment temperature and time, the crystallinity of the NaYP2O7 glass–ceramics increases, while the transmittance gradually decreases. The optimal heat‐treatment regime is identified to be crystallized over 4 h at 580°C based on the crystallinity and transmittance. Under the excitation of 408 nm, both the Mn2+‐doped precursor glass and glass–ceramic crystallized at 580°C for 4 h generate a broad emission at 620 nm (4T2(g)→6A1(s)) with a full width at half‐maximum (FWHM) of ∼107 nm. The glass–ceramics exhibit higher emission intensity and longer decay lifetime than that of precursor glass with the aid of the low phonon energy NaYP2O7 crystals. The Mn2+‐doped glass–ceramic exhibits stable orange‐red luminescence with the chromaticity coordinates of (0.568, 0.428), low correlation color temperature of 1 800 K, high color purity of 98.88%, and low thermal quenching (70% at 373 K of the initial intensity at 298 K). The above results indicate that Mn2+‐doped transparent NaYP2O7 glass–ceramics have promising potential for orange‐red color display devices.
materials science, ceramics