Self‐reduction triggered color tuning of Eu3+‐doped aluminosilicate glass for solid‐state white illumination
Hang Chen,Chunming Zhou,Xu Chen,Chang Min,Shenghui Lin,Yanbin Li,Tianyuan Zhou,Jian Kang,Chaofan Shi,Cen Shao,Pengde Han,Wieslaw Strek,Hao Chen,Le Zhang
DOI: https://doi.org/10.1111/jace.20237
IF: 4.186
2024-11-07
Journal of the American Ceramic Society
Abstract:Rare earth‐doped transparent glass, boasting high transmittance and excellent luminescent properties, holds great potential in the field of all‐inorganic solid‐state white illumination. Currently reported single‐structure solid‐state white lighting usually has the problems of low color rendering index (CRI) and high correlated color temperature (CCT) due to the lacking of red light emission. In this work, a novel single‐structure MgO–Al2O3–SiO2–Eu2O3 (MAS: Eu) glass with color tuning was prepared by the simple glass melting process. Interestingly, the prepared Eu3+‐doped aluminosilicate glass possessed a unique capability to achieve color emission under different excitation wavelengths. The reason for this was attributed to the good self‐reduction capability of the MAS glass, which effectively reduced Eu3+ to Eu2+ under an air atmosphere. Meanwhile, only by regulating the Eu3+ doping concentration, the MAS glass also achieved a tunable emission from blue to white to red light under 380 nm excitation. The acquisition of white light was realized through the multispectral emission of blue–green light emitted by Eu2+ and orange–red light emitted by Eu3+. Remarkably, the single‐structure MAS glass doped with 8 wt.% Eu3+ successfully achieved high‐quality white light and high thermal stability, exhibiting a high CRI of 86, a low CCT of 2761 K, good chromaticity parameters of (0.407 and 0.3192), and the emission intensity at 423 K remains above 86.35% that of room temperature. Meanwhile, the doped Eu3+ exceeded 12 wt.%, without any observable concentration quenching. Moreover, the MAS: Eu glass showed a high transmittance of 90 and a moderate thermal conductivity of 1.45 W/mK (epoxy resin ∼0.17 W/mK). These results would dramatically inspire the development of high‐quality solid‐state white lighting applications.
materials science, ceramics