Abstract:For development of thin bioactive coatings on metal implants, a dense and uniform apatite layer was coated onto titanium (Ti) implants in situ by using a new biomimetic method, which is composed of apatite nucleation and growth steps in simulated body fluid (SBF). Analysis of the coatings by thin film X-ray diffraction and scanning electron microscopy-energy dispersive X-ray microanalysis (SEM-EMPA) before implantation showed that its characteristics were very similar to those of natural bone. The coated and uncoated rectangular plates were bilaterally implanted into the tibial proximal metaphyses of rabbits. After 6, 10 and 25 weeks post-implantation, the bone bonding and bone formation at the bone-implant interfaces were evaluated by a detachment test and undecalcified histological examination. Mechanical testing in tension showed that the failure load of apatite layer-coated Ti implants was significantly higher than that of uncoated control at each time period (all P < 0.001). Histologically, it was shown that bone was deposited directly onto the apatite coating without any intervening soft tissue, while in the paired controls, interpositional soft tissue was seen at the bone-implant interface. By SEM-EPMA, a uniform calcium- and phosphorus-rich layer was detected between the coated implants and bone, but not in uncoated controls at either earlier or later time periods. The results indicate that the apatite layer deposited on Ti in situ may significantly increase the bone bonding strength by providing a bioactive surface, which allows for an early bone apposition to the implant. In addition, the apatite layer-coated Ti produced by the biomimetic process may fulfil the requirements of favourable thin coatings and strong adhesion at the metal-coating interface.

Apatite Formation on Poly(aryl Ether Sulfone Ketone) Surfaces by Means of Polydopamine Layers Functionalized with Phosphonate Groups

Improving Hydrophilicity and Inducing Bone-Like Apatite Formation on PPBES by Polydopamine Coating for Biomedical Application

Phosphonate-Functionalized Poly(phthalazinone Ether Ketones) Induce the Formation of Apatite Coatings for Enhanced Biocompatibility and Osteogenic Activity

Apatite Formation Induced by Chitosan/Gelatin Hydrogel Coating Anchored on Poly(aryl ether nitrile ketone) Substrates to Promote Osteoblastic Differentiation

Bone-like apatite coating on functionalized poly(etheretherketone) surface via tailored silanization layers technique

Apatite Layer-Coated Titanium for Use As Bone Bonding Implants

Stabilization of Apatite Coatings on PPENK Surfaces by Mechanical Interlocking to Promote Bioactivity and Osseointegration In Vivo

In vitro apatite formation on porous anodic alumina induced by a phosphorylation treatment

Enhancing Tissue Adhesion and Osteoblastic Differentiation of MC3T3-E1 Cells on Poly(aryl Ether Ketone) by Chemically Anchored Hydroxyapatite Nanocomposite Hydrogel Coating.

Preparation and Biocompatibility of Polydopamine Modified Porous Polyetheretherketone Implants

A two-step strategy to deposit a hydroxyapatite coating on polydopamine-coated polymer fibers

Enhanced Adsorption Stability and Biofunction Durability with Phosphonate-Grafted, PEGylated Copolymer on Hydroxyapatite Surface.

Polydopamine-functionalized polymer particles as templates for mineralization of hydroxyapatite: Biomimetic and in vitro bioactivity

Effects of Structure and Composition of the CaP Composite Coatings on Apatite Formation and Bioactivity in Simulated Body Fluid

Effect of Hydrolysis Pretreatment on the Formation of Bone-like Apatite on Poly(L-lactide) by Mineralization in Simulated Body Fluids

Regulation of Surface Micro/nano Structure and Composition of Polyetheretherketone and Their Influence on the Behavior of MC3T3-E1 Pre-Osteoblasts.

Formation of Bone-Like Apatite on Poly(l-Lactide) to Improve Osteoblast-Like Compatibility in Vitro and in Vivo

Surface Processing Technology of Apatite Coating of on Bone Tissue Engineering Scaffolds of Poly (lactic Acid)

Mussel-Inspired Polydopamine Coating: A General Strategy to Enhance Osteogenic Differentiation and Osseointegration for Diverse Implants.

Polydopamine-Assisted Surface Modification for Bone Biosubstitutes

BIOACTIVE HYDROXYAPATITE COATING ON POLYAMIDES IMPLANT