Abstract:Ti6Al4V (TC4) alloy has been widely applied in the military, industrial, chemical, and medical fields due to their excellent thermal stability, corrosion resistance , and biocompatibility. However, titanium alloys are notorious for their poor tribological properties, such as their high friction coefficients and low surface bearing capacities. To tackle this problem, combination of laser surface texturing (LST) and double glow plasma chromizing was conducted to improve the wear resistance of TC4. LST was first conducted to produce uniform dimples with a diameter of 300 μm and gradient density of 11 % on the Ti6Al4V substrate. A chromizing coating (Cr-coating) was subsequently deposited on the surfaces of the textured and raw Ti6Al4V alloy by double glow plasma surface alloying (DGPSA). A continuous and compact Cr-coating with a thickness of about 55 μm was formed on TC4 after being maintained at a temperature of 850 °C, and the coating was mainly composed of a solid solution and intermetallic compounds of Cr 2 Ti phases. The surface hardness after alloying was two times higher than that of the TC4 substrate. Comparative assessments on the wear resistance of the Cr-coatings with and without LST treatment and the TC4 alloy were carried out using a ball-on-disk wear tester. The results showed that the mass loss and specific wear rate of the duplex-treated sample were 1.54 mg and 7.14 × 10 −4 mm 3 ·N −1 ·m −1 . The mass loss and specific wear rate of the TC4 were 4.32 mg and 1.62 × 10 −3 mm 3 ·N −1 ·m −1 . The specific wear rates of the four tested samples were in the following order: the duplex-treated TC4 < textured TC4 < chromized TC4 < polished TC4. The coating obtained by LST-double glow plasma chromizing duplex treatment exhibited an outstanding durability and the best mechanical performance. Thus, this approach be used for the protection of Ti6Al4V surface in engineering components and medical instruments.

Comparison of the Effect of Typical Patterns on Friction and Wear Properties of Chromium Alloy Prepared by Laser Surface Texturing

Combined Effect of a Laser Cladded Coating and Surface Texture on Tribological Performance Under Dry Sliding and Starved Lubrication

Effect of ion beam etching on the tribological performance of laser textured Co-Cr-Mo alloy

The Friction And Wear Behavior Of Laser Textured Surfaces In Non-Conformal Contact Under Starved Lubrication

Effects of Laser Surface Texturing and Lubrication on the Vibrational and Tribological Performance of Sliding Contact

Analysis of synergistic friction reduction effect on micro-textured cemented carbide surface by laser processing

Optimization of Tribological Characteristics of a Combined Pattern Textured Surface Using Taguchi Design

An Experimental Investigation of Tribological Performance of Triangular Textures in Water Lubrication Regime

Laser Melting and Surface Texture Technology: Effect on Friction Properties

Additional Tribological Effect of Laser Surface Texturing and Diamond-Like Carbon Coating for Medium Carbon Steel at Near Room Temperature

Growth characteristics and wear properties of micro-arc oxidation coating on Ti-6Al-4V with different laser texture shapes

Influence of Micro-Texture on the Tribological Behavior of WC/MoS2/Fe-Based Alloy Coating by Laser Cladding

Anti-Wear Property of Laser Textured 42CrMo Steel Surface

Tribological Properties of Ti6Al4V Alloy Composite Texture Fabricated by Ultrasonic Strengthening Grinding and Laser Processing

Friction and wear characteristics modification via laser surface textured grooves

Combining laser surface texturing and double glow plasma surface chromizing to improve tribological performance of Ti6Al4V alloy

Surface Texturing for Low Friction Mechanical Components

Tribological behavior of zirconia ceramic with micro-channels produced by nanosecond laser

Ultra-low wear of titanium alloy surface under lubricated conditions achieved by laser texturing and simultaneous nitriding

Effect of Nanosecond Laser Texturization on Tribological Behavior of AISI 321 Stainless Steel

Effect and performance analysis of different surface treatments on polymer-metal friction pairs