Cellulose triacetate (CTA)-based forward osmosis membranes for water purification: optimization of dope solution composition and preparation conditions

Huaqiang Chu,Wenwen Zhang,Lin Wang,Xi Wei,Zhenjiang Yu,Yalei Zhang,Xuefei Zhou
DOI: https://doi.org/10.5004/dwt.2018.21891
IF: 1.1
2018-01-01
Desalination and Water Treatment
Abstract:In this study, different PET support fabric based forward osmosis (FO) membranes were prepared and the optimal casting compositions as well as preparation conditions were investigated. The results showed that the optimal membrane casting solution compositions were 10.9% wt. CTA, 79.6% wt. solvents (the ratio of 1,4-dioxane and acetone is 6), (1,4-dioxane/acetone = 6/1), and 9.5% wt. additives (2.0% wt. PVP and 7.5% wt. lactic acid). In addition, the active layer formation was largely dependent on the thickness and pore size of PET support and the membrane on an 80-mu m-thick PET support fabric with a pore size of 80 mu m presented the best performance. Evaporation time, environmental humidity, annealing temperature and annealing time also played important roles on the membrane flux and reverse salt flux control. Experimental results found that high environmental humidity and a relatively low annealing temperature of 45 degrees C was optimal for this work. The optimized membrane showed lower salt leakage than commercial HTI membrane. This lab-scale FO membrane with high salt rejection ratio and low back diffusion rate could provide a great option for a method of desalination and the detail influence of different casting compositions as well as preparation conditions on membrane performance present significant impacts on the industrial production of FO membrane.
What problem does this paper attempt to address?