Fabrication and Performance of Cellulose Acetate Membranes for Forward Osmosis

李国亮,王军,赵长伟,侯得印,刘会娟

DOI: https://doi.org/10.16159/j.cnki.issn1007-8924.2017.01.015

2017-01-01

Abstract:A cellulose acetate forward osmosis (FO) membrane enhanced by polyethylene terephthalate (PET) mesh was fabricated via a phase inversion process.The obtained PET mesh embedded membrane shows asymmetric structure with the thickness of 127 μm.The mechanical strength is as high as 37.86 N.The high hydrophilic membrane has a contact angle of 51.4°,and the porosity reaches to 74.2％.The membrane performance shows long term stability after being immersed in the solutions with the pH in the range of 2 to 11.The membrane has a well organic fouling resistance and the permeability can be completely recovered by simple cleaning.The performance of the membrane was tested using 0.2 mol/L NaCl as the feed solution and 1.5 mol/L glucose as the draw solution.The membrane displayed a water flux of 3.78 L/(m2 · h) and salt rejection of 95.65 ％ in forward osmosis mode.While in pressure retarded osmosis (PRO) mode,the water flux was 5.34 L/(m2 · h) and salt rejection 96.25％.The high ratio (0.71) of water flux in the mode of FO in that of PRO indicates that the fabricated membrane has a lower degree of internal concentration polarization(ICP).