Zwitterionic forward osmosis membrane with low structural parameter based on highly porous polyvinylidene fluoride substrate for desalination

Li-Jing Zhu,Yi-Ning Hu,Yi Wang,Yan-Feng Guo,Zhi-Xiang Zeng

DOI: https://doi.org/10.1016/j.mtcomm.2022.104344

IF: 3.8

2022-09-03

Materials Today Communications

Abstract:Polyamide thin-film composites (PA-TFC) forward osmosis (FO) membranes have great potential in wastewater treatment and desalination. However, they are continuously studied to further enhance the FO performances from the improvement of the PA layer and the substrate individually. Here, a polyvinylidene fluoride/poly(hydroxyethyl methacrylate) (PVDF/PHEMA) membrane with a highly porous surface was fabricated and used as the substrate to engineer a thin and rough PA layer. After being post-modified by zwitterionic groups, the resulting membrane (namely TFC90-Z) has a much lower structure parameter ( S , 216 ± 12 μm) in comparison to common FO membranes in literature, thus decreasing internal concentration polarization and increasing FO performances. Specific salt flux ( J s /J w ) and water flux ( J w ) of TFC90-Z are 0.03 ± 0.01 g/L and 18.5 ± 0.4 L m −2 h −1 under the active layer-facing draw solution (AL-DS) orientation using 1.0 M NaCl as the draw solution and deionized water as the feed solution. Meanwhile, NaCl rejection is 91.6 ± 0.1 %. This work offers an efficient way to engineer excellent PA-TFC FO membranes for aqueous separation and desalination.

materials science, multidisciplinary